CORROSION INHIBITION OF LOW PHOSPHONIC MULTIPOLYMER WATER TREATMENT AGENT TO BRASS
摘 要
通过静态腐蚀实验和表面元素分析及电化学方法研究了低磷共聚物在循环冷却水中对黄铜的缓蚀作用.结果表明,低磷共聚物在水溶液中的浓度为8 mg/L时,对黄铜的缓蚀率为70.2%.低磷共聚物在水溶液中对黄铜的缓蚀机理是共聚物在试片表面活性位置的吸附抑制了阳极电化学过程的结果.
Abstract
A low phosphonic multipolymer was synthesized and its corrosion inhibition efficiency to brass in a synthetic water was investigated.The results of weight loss measurements showed the inhibition efficiency was 702%,when the concentration of the low phosphonic multipolymer inhibitor in the synthetic water was 8mg·L-1.The element analysis at the surface of brass specimens and electrochemical tests showed that the inhibitive mechanism of the multipolymer was to inhibit the anodic reaction mainly due to chemical adsorption of the multipolymer inhibitor on active places of the brass specimen surface.
中图分类号 TG174.42
所属栏目 试验研究
基金项目
收稿日期 2005/9/21
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: WANG Chen,SONG Cun-yi,CHEN Yue-fang. CORROSION INHIBITION OF LOW PHOSPHONIC MULTIPOLYMER WATER TREATMENT AGENT TO BRASS[J]. Corrosion & Protection, 2006, 27(7): 346~348
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】全国化学标准化技术委员会水处理剂分会编.循环冷却水水质及水处理剂标准应用指南[M].北京:化学工业出版社,2003.156-159.
【2】王吉会,姜晓霞,李诗卓.表面膜对含硼HA177-2黄铜腐蚀的影响[J].材料研究学报,1997,11(3):292-296.
【3】汪的华,邹津耘,邱万川,等.黄铜脱锌的抑制[J].应用化学,1997,14(5):104-106.
【4】曹楚南.腐蚀电化学[M].北京:化学工业出版社,1994.28-31.
【5】梅平,艾俊哲,陈武,等.抑制二氧化碳腐蚀的缓蚀剂及其缓蚀机理研究[J].石油学报,2004,25(5):104-107.
【2】王吉会,姜晓霞,李诗卓.表面膜对含硼HA177-2黄铜腐蚀的影响[J].材料研究学报,1997,11(3):292-296.
【3】汪的华,邹津耘,邱万川,等.黄铜脱锌的抑制[J].应用化学,1997,14(5):104-106.
【4】曹楚南.腐蚀电化学[M].北京:化学工业出版社,1994.28-31.
【5】梅平,艾俊哲,陈武,等.抑制二氧化碳腐蚀的缓蚀剂及其缓蚀机理研究[J].石油学报,2004,25(5):104-107.
相关信息