江苏油田韦2块集输管线腐蚀原因分析与对策

CORROSIVE CAUSE ANALYSIS AND PROTECTION MEASURES OF OIL GATHERING TRANSPORTATION PIPELINE IN JIANGSU OIL FIELD

缪建成

马惠

沈晓翔

汤元春

黄一汉

摘要

通过对韦2块采出水和腐蚀产物的分析以及对管材的分析,认为集输管线的腐蚀与水中硫化物含量高,以及碳酸氢盐较高,电导率高有关.分析认为,在现有的几种防护方法中,较好的是添加缓蚀剂并对管内壁采用防腐蚀涂层的方法.

标签硫化物

防护

水分析

集输管线

腐蚀产物

Sulfide

Protection

Water analysis

Oil gatherig transportation pipeline

Corrosion product

Abstract

Extracted water,corrosion product and tubing materical were analyzed.The main corrosive factor of oil gathering transportation pipeline was sulfide.Compared with other anticorrosive methods,the application of inhibitors and anticorrosive coatings was better ways.

中图分类号 TE988.2

所属栏目应用技术

基金项目

收稿日期 2006/1/11

修改稿日期 2006/3/20

网络出版日期

作者单位点击查看

引用该论文: MIAO Jian-cheng,MA Hui,SHEN Xiao-xiang,TANG Yuan-chun,HUANG Yi-han. CORROSIVE CAUSE ANALYSIS AND PROTECTION MEASURES OF OIL GATHERING TRANSPORTATION PIPELINE IN JIANGSU OIL FIELD[J]. Corrosion & Protection, 2006, 27(11): 571～573

论文评价

共有人对该论文发表了看法，其中：

人认为该论文很差

人认为该论文较差

人认为该论文一般

人认为该论文较好

人认为该论文很好

分享论文

相关信息

	标题	相关频次
	某油田N80钢油管腐蚀失效的原因	4
	“华光礁Ⅰ号”沉船出水铜钱的腐蚀情况	2
	304、316不锈钢和Inconel 617镍基合金在硝酸熔盐中的腐蚀行为	2
	304不锈钢大小头短期内开裂原因分析	2
	316NG不锈钢在高纯水环境中的腐蚀行为	2
	3A12、5052、6063铝合金在沿海大气环境中的腐蚀行为	2
	3A21铝合金在乙二醇水溶液中的腐蚀行为	2
	40Cr钢油缸断裂原因	2
	48MnV非调质钢曲轴断裂的原因分析	2
	CO₂/H₂S分压比对BG90SS材质腐蚀行为的影响	2
	CO₂驱采出井井下附件材料的腐蚀评价与优选	2
	EH36级平台钢耐海洋大气腐蚀性能	2
	P110S钢级油管断裂失效分析	2
	P110钢和TP110SS钢在含不同饱和气体NaCl溶液中的腐蚀行为	2
	PTA装置碱洗对设备腐蚀开裂影响讨论	2
	Q345B中厚钢板分层缺陷的形成原因	2
	SS411NS型杀菌剂对Q235钢在循环冷却水中腐蚀行为的影响	2
	X100管线钢在库尔勒土壤模拟溶液中的腐蚀行为	2
	X80管线钢在库尔勒土壤模拟溶液中的腐蚀行为	2
	X80管线钢在水饱和碱性沙土中的腐蚀行为	2
	胺液脱硫系统腐蚀与防护的研究现状	2
	长庆油田含硫化氢区块中J55钢套管的腐蚀机理	2
	长庆油田集输系统管道防腐蚀工艺研究	2
	超高强钢FG20在不同pH高含硫油田水中的腐蚀行为	2
	超临界CO₂输送环境中O₂、SO₂和NO₂杂质对X52钢腐蚀行为的影响	2
	超临界火电厂海水循环水泵的防腐蚀方案	2
	船用海水过滤器的腐蚀和防护	2
	纯H₂S环境中腐蚀产物离子选择性对P110S低合金钢腐蚀行为的影响	2
	大牛地气田某输气管道内腐蚀的原因	2
	氮化处理的贫铀表面在盐雾环境中的腐蚀行为	2