BTA和HMMP对X70钢在含H2S弱酸性溶液中的缓蚀作用
INHIBITION OF BTA AND HMMP TO X70 STEEL IN H2S WEAK ACIDIC SOLUTION
摘 要
采用静态失重、交流阻抗、动电位扫描及扫描电镜法研究了苯并三氮唑(BTA)在单独使用时和与6甲基-2巯基-4羟基嘧啶(HMMP)复配后对X70钢在含H2S弱酸性溶液中的缓蚀作用.结果表明,BTA属于以抑制阳极过程为主的混合型缓蚀剂,在所研究的浓度范围内,随其浓度的增大,缓蚀率逐渐增大；BTA和HMMP复配后有缓蚀协同效应,复配的最佳浓度值为100mg/L,最佳浓度比为3∶1.
HMMP
X70钢
缓蚀
BTA
HMMP
X70 steel
Inhibition
Abstract
The inhibitive effect of benzotriazole (BTA) and synergistic inhibitive effect of BTA and 4-hydroxy-2-mercapto-6-methyl-primidine (HMMP) on the corrosion of X70 steel in H2S weak acidic solution was studied by means of static weight loss,potentiodynamic polarization curves,electrochemical impendence spectroscopy and scanning electron microscopy.HMMP was a mixed inhibitor that mainly restrain the anodic process,the inhibition increased gradually with the increasing of its concentration within the range of concentration studied.A synergistic inhibitive effect of BTA and HMMP combined inhibitors on the corrosion of X70 steel was observed.The optimal concentration was 100mg/L and the optimal concentration ratio was 3∶1.
中图分类号 TG174.42
所属栏目 试验研究
基金项目 四川省科技厅应用基础研究重点项目(04JY029-100)
收稿日期 2006/5/17
修改稿日期 2006/7/7
网络出版日期
作者单位点击查看
引用该论文: GUO Hong,WANG Ying,HE Xiao-ying. INHIBITION OF BTA AND HMMP TO X70 STEEL IN H2S WEAK ACIDIC SOLUTION[J]. Corrosion & Protection, 2006, 27(12): 604～607
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李云涛,杜则裕,陶勇寅,等.X70管线钢硫化氢应力腐蚀[J].焊接学报,2003,24(3):75-78.
【2】Subramanyan N C,Mayanns S M.Azoles as corrosion inhibitors for mile steel in alkaline mine warer[J].Corrosion Science,1985,25(3):163-169.
【3】杨植震,白 梁.铁器文物的缓蚀研究(1)——苯并三氮唑对低碳钢的缓蚀作用[J].复旦学报(自然科学版),1994,33(5):584-590.
【4】郭红,何晓英.X70钢在含H2S弱酸性溶液中的防腐研究[J].中国腐蚀与防护学报,2006,26(6):350-355.
【5】曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002.53.
【6】杨昌柱,张敬东.新型高效缓蚀剂DLY对碳钢和铜的缓蚀作用[J].材料保护,2001,34(1):25-26.
【7】杨怀玉,陈家坚,曹楚南,等.H2S水溶液中的腐蚀与缓蚀作用机理的研究Ⅶ-H2S溶液中咪唑啉衍生物对碳钢腐蚀电极过程的影响[J].中国腐蚀与防护学报,2002,22(6):321-325.
【8】王佳,曹楚南.缓蚀剂阳极脱附现象的研究Ⅱ——缓蚀剂阳极脱附对电极阻抗的影响[J].中国腐蚀与防护学报,1995,15(4):247-253.
【2】Subramanyan N C,Mayanns S M.Azoles as corrosion inhibitors for mile steel in alkaline mine warer[J].Corrosion Science,1985,25(3):163-169.
【3】杨植震,白 梁.铁器文物的缓蚀研究(1)——苯并三氮唑对低碳钢的缓蚀作用[J].复旦学报(自然科学版),1994,33(5):584-590.
【4】郭红,何晓英.X70钢在含H2S弱酸性溶液中的防腐研究[J].中国腐蚀与防护学报,2006,26(6):350-355.
【5】曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002.53.
【6】杨昌柱,张敬东.新型高效缓蚀剂DLY对碳钢和铜的缓蚀作用[J].材料保护,2001,34(1):25-26.
【7】杨怀玉,陈家坚,曹楚南,等.H2S水溶液中的腐蚀与缓蚀作用机理的研究Ⅶ-H2S溶液中咪唑啉衍生物对碳钢腐蚀电极过程的影响[J].中国腐蚀与防护学报,2002,22(6):321-325.
【8】王佳,曹楚南.缓蚀剂阳极脱附现象的研究Ⅱ——缓蚀剂阳极脱附对电极阻抗的影响[J].中国腐蚀与防护学报,1995,15(4):247-253.
相关信息