复合常温磷化促进剂研究
COMPOUND PHOSPHATING ACCELERATORS AT ROOM TEMPERATURE
摘 要
锌系中温磷化中常用的加速剂亚硝酸钠加速作用较好,但其分解产生的NOX毒性较大.为此研制了一种含硝酸胍和氯酸钠的复合促进剂,考察了复合促进剂所含物质对磷化液磷化效果的影响,对其作用机理进行了讨论.该磷化液在25～35 ℃,10～15 min时,能在碳钢表面形成一层致密均匀的磷化膜,经测试,其耐蚀性能优良.
常温
复合促进剂
Zinc phosphating
Room temperature
Compound accelerator
Abstract
For the shortcomings of zinc phosphating technology at room temperature,a quick phosphating solution which does not contain nitrite has been developed.The effect of the accelerators in phosphating solution on phosphatization was investigated.The reaction mechanism was also studied.The phosphating coating achiered in the phosphating solution at 25～35 ℃ for 10～15 min could had a good performance.
中图分类号 TG178
所属栏目 应用技术
基金项目 河南省自然科学研究项目(200460178);河南省科技攻关研究项目(0424240074)
收稿日期 2006/3/31
修改稿日期 2006/5/21
网络出版日期
作者单位点击查看
引用该论文: ZHANG Sheng-lin,KONG Xiao-bo,ZHANG Ming-ming,CHEN Hua-hui. COMPOUND PHOSPHATING ACCELERATORS AT ROOM TEMPERATURE[J]. Corrosion & Protection, 2007, 28(3): 126～128
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】俞敦义,殷宏飞.室温磷化液的研究[J].表面技术,1994,23(1):16-17.
【2】黄霓裳,郭良生.室温磷化加速剂的选择[J].表面技术,1996,25(4):19-21.
【3】刘娅莉.磷化技术的最新进展[J].电镀与涂饰,1998,17(4):44-49.
【4】张圣麟,陈华辉,李红玲,等.常温磷化处理技术的现状及展望[J].材料保护,2006,39(7):42-47.
【5】鲁维国,李淑英.磷化促进剂[J].表面技术,2002,31(6):12-14.
【6】张圣麟,李红玲,郑红河,等.常温铁系磷化工艺研究[J].腐蚀与防护,2006,27(3):156-158.
【2】黄霓裳,郭良生.室温磷化加速剂的选择[J].表面技术,1996,25(4):19-21.
【3】刘娅莉.磷化技术的最新进展[J].电镀与涂饰,1998,17(4):44-49.
【4】张圣麟,陈华辉,李红玲,等.常温磷化处理技术的现状及展望[J].材料保护,2006,39(7):42-47.
【5】鲁维国,李淑英.磷化促进剂[J].表面技术,2002,31(6):12-14.
【6】张圣麟,李红玲,郑红河,等.常温铁系磷化工艺研究[J].腐蚀与防护,2006,27(3):156-158.
相关信息