微量元素对1050铝基PS版电蚀性能的影响
EFFECTS OF MICROELEMENTS ON ELECTROLYSIS PROPERTIES OF 1050 ALUMINIUM SUBSTRATE PS PLATE
摘 要
研究了Mg、Mn含量对PS版电蚀性能的影响.利用电化学测试仪、扫描电镜及能谱仪检测分析了不同Mg、Mn含量的PS版电解腐蚀速率和腐蚀均匀性的差异.分析表明,Mg含量从0.001％提高到0.10％时,Mg更多地富集于铝板表面,形成微小的易腐蚀的含Mg复合氧化物颗粒,促进腐蚀,进而提高板基的腐蚀速率；Mn含量的增加能提高Mg元素在板基表面的分布均匀性,减少Fe元素在铝板表面的富集,降低Fe对腐蚀均匀性的危害.
电解腐蚀
1050铝合金
镁
锰
PS plate
Electrolytic corrosion
1050 aluminum alloy
Mg
Mn
Abstract
The effects of microelements on the electrolysis properties of 1050 aluminium substrate PS plate were investigated by means of electrochemical testing and SEM(EDX).The difference of corrosion rate and uniformity of the PS plates with different contents of Mg and Mn was compared.When the content of Mg increased from 0.001％ to 0.10％,Mg was enriched more to the surface of aluminum plate and formed fine compound-oxide grains,resulting in accelerated corrosion.With the increase of content of Mn,the distribution uniformity of Mg at the surface of plate was improved,the of Fe in the surface decreased,the damage of Fe to the corrosion uniformity of PS plate was reduced.
中图分类号 TG172.6
所属栏目 试验研究
基金项目
收稿日期 2006/4/27
修改稿日期 2006/5/27
网络出版日期
作者单位点击查看
引用该论文: LI Hong-ying,WANG Chang-jian,ZENG Zai-de. EFFECTS OF MICROELEMENTS ON ELECTROLYSIS PROPERTIES OF 1050 ALUMINIUM SUBSTRATE PS PLATE[J]. Corrosion & Protection, 2007, 28(4): 194～197
被引情况:
【1】毛大恒,杨栋, "进口与国产PS版用铝板组织与性能的对比",机械工程材料 33, 40-44(2009)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】卜柏林,陈小青.铝合金PS版的生产工艺及发展趋势[J].铝加工,1994,17(6):30-36.
【2】高作文,梁岩,王琦.国内外PS版用铝板基综合测试与分析[J].轻合金加工技术,2001,29(5):26-30.
【3】袁朴,岳德茂,朱廷凯,等.PS版技术及应用[M].北京: 印刷工业出版社,1994:67-120.
【4】冯云祥.铝板基质量对印刷用PS版质量的影响[J].铝加工,1999,22(2):44-49.
【5】王祝堂.铝基PS版生产及其再生工艺(1)[J].轻合金加工技术,1995,23(6):33-39.
【6】Van Alphen L,Nauwen P,Slakhorst J.The relationship between the composition,the structure parameters and the etchability of alloyed Al-cathode foil for elctolytic capacitors[J].Z Metallkde,1979,70(3):158-167.
【7】徐进,毛卫民,冯惠平,等.Cu对高压电解电容器阳极铝箔再结晶织构的影响[J].北京科技大学学报,2002,24(2):133-136.
【8】张承忠.金属的腐蚀与保护[M].北京: 冶金工业出版社,2000:50-90.
【9】姜应律,吴荫顺.用极化曲线研究钛合金在水、醇中腐蚀机理的差异[J].腐蚀科学与防护技术,2005,17(3):154-159.
【10】Van Alphen L,Nauwen P,Slakhorst J.The relationship between the composition,the structure parameters and the etchability of alloyed Al-cathode foil for elctolytic capacitors[J].Z Metallkde,1979,70(3):158-167.
【11】王祝堂,田荣璋.铝合金及其加工手册[M].长沙: 中南大学出版社,2000:156-186.
【12】Arai K,Suzuki T,Atsumi T.Effect of trace elements on etching of aluminum electrolytic capacitor foil[J].Journal of the Electrochemical Society,1985,132(7):1667-1671.
【13】陈国光,曹婉真.电解电容器[M].西安: 西安交通大学出版社,1993:81-106.
【14】李劲风,郑子樵.第二相在铝合金局部腐蚀中的作用机制[J].材料导报,2005,19(2):81-90.
【15】王祝堂,田荣璋.铝合金及其加工手册[M].长沙: 中南大学出版社,2000:46-57.
【2】高作文,梁岩,王琦.国内外PS版用铝板基综合测试与分析[J].轻合金加工技术,2001,29(5):26-30.
【3】袁朴,岳德茂,朱廷凯,等.PS版技术及应用[M].北京: 印刷工业出版社,1994:67-120.
【4】冯云祥.铝板基质量对印刷用PS版质量的影响[J].铝加工,1999,22(2):44-49.
【5】王祝堂.铝基PS版生产及其再生工艺(1)[J].轻合金加工技术,1995,23(6):33-39.
【6】Van Alphen L,Nauwen P,Slakhorst J.The relationship between the composition,the structure parameters and the etchability of alloyed Al-cathode foil for elctolytic capacitors[J].Z Metallkde,1979,70(3):158-167.
【7】徐进,毛卫民,冯惠平,等.Cu对高压电解电容器阳极铝箔再结晶织构的影响[J].北京科技大学学报,2002,24(2):133-136.
【8】张承忠.金属的腐蚀与保护[M].北京: 冶金工业出版社,2000:50-90.
【9】姜应律,吴荫顺.用极化曲线研究钛合金在水、醇中腐蚀机理的差异[J].腐蚀科学与防护技术,2005,17(3):154-159.
【10】Van Alphen L,Nauwen P,Slakhorst J.The relationship between the composition,the structure parameters and the etchability of alloyed Al-cathode foil for elctolytic capacitors[J].Z Metallkde,1979,70(3):158-167.
【11】王祝堂,田荣璋.铝合金及其加工手册[M].长沙: 中南大学出版社,2000:156-186.
【12】Arai K,Suzuki T,Atsumi T.Effect of trace elements on etching of aluminum electrolytic capacitor foil[J].Journal of the Electrochemical Society,1985,132(7):1667-1671.
【13】陈国光,曹婉真.电解电容器[M].西安: 西安交通大学出版社,1993:81-106.
【14】李劲风,郑子樵.第二相在铝合金局部腐蚀中的作用机制[J].材料导报,2005,19(2):81-90.
【15】王祝堂,田荣璋.铝合金及其加工手册[M].长沙: 中南大学出版社,2000:46-57.
相关信息