MORPHOLOGY AND CORROSION RESISTANCE OF MECHANICALLY PLATED COATINGS
摘 要
分别用325、800目颗粒状锌粉或325目锌粉+10%铝粉球磨成的片状复合粉,在促进剂作用下,形成三种机械镀层.用SEM法测定了金属原料粉及镀层的SEM形貌;用盐雾试验测定了镀层的耐蚀性.试验结果表明:片状锌-铝复合粉形成的镀层综合性能优于800目粒状锌粉形成的镀层.另外,随着金属粉粒度的减小、铝粉的添加及片状化处理,使镀层的光亮度、密实度和耐腐蚀性明显提高.
Abstract
Three kinds of mechanically plated coatings,which were made up of 325 mesh spherical zinc powders or 800 mesh spherical zinc powders or 325 mesh grain zinc powders and grain aluminum powders (10wt%),were formed with flaky compound powders respectively with the help of the precipitant.The morphology of the metal material powders and mechanically plated coatings were examined by SEM.The corrosion resistance of the mechanically plated coatings was evaluated by the salt spray test.The comprehensive properties of the mechanically plated coatings formed with zinc-aluminum flaky compound powders were better than those formed with 800 mesh spheric zinc powders.In addition,with the decrease of grain size,addition of aluminum powers and flaky treatment,the brightness,density and corrosion resistance of the mechanically plated coatings were enhanced.
中图分类号 TG174.44
所属栏目 试验研究
基金项目
收稿日期 2007/1/9
修改稿日期 2007/2/5
网络出版日期
作者单位点击查看
引用该论文: BA Xiao-ge,ZHAO Zeng-dian,DING Jin-cheng. MORPHOLOGY AND CORROSION RESISTANCE OF MECHANICALLY PLATED COATINGS[J]. Corrosion & Protection, 2007, 28(6): 293~295
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】丁金城,赵增典,毕玉遂,等.高强度螺栓机械镀锌常见问题处理[J].山东工程学院学报,2000,14(2):59-61.
【2】赵增典,于先进,丁金城,等.机械镀镀层制备及性能研究[J].腐蚀科学与防护技术,2006,6(3):206-208.
【3】Rochester, Thomas H.Process of mechanical plating[P].US No 5,762,942.
【4】赵增典,于先进,丁金城,等.机械镀锌和锌铝镀层的形貌及耐蚀性[J].金属热处理,2006,31(8):21-24.
【5】赵增典,丁金城,于先进,等.锌铬膜技术的研究及现状[J].山东工程学院学报,2002(6):35.
【2】赵增典,于先进,丁金城,等.机械镀镀层制备及性能研究[J].腐蚀科学与防护技术,2006,6(3):206-208.
【3】Rochester, Thomas H.Process of mechanical plating[P].US No 5,762,942.
【4】赵增典,于先进,丁金城,等.机械镀锌和锌铝镀层的形貌及耐蚀性[J].金属热处理,2006,31(8):21-24.
【5】赵增典,丁金城,于先进,等.锌铬膜技术的研究及现状[J].山东工程学院学报,2002(6):35.
相关信息