不锈钢作为给水材料在含Cl-水中的腐蚀行为
CORROSION BEHAVIOR OF STAINLESS STEEL 304 AS WATER SUPPLY MATERIAL IN WATER CONTAINING CHLORIDE
摘 要
采用浸泡试验结合极化曲线以及电化学阻抗测试研究了304不锈钢在含不同浓度Cl-的水溶液中的腐蚀行为.结果表明引起304不锈钢产生明显点蚀的NaCl浓度为0.4%；随Cl-浓度和温度的升高,点蚀现象加重；点蚀电位与温度之间存在一线性关系；阻抗谱测试也显示出NaCl浓度大于0.4%后对钝化膜的破坏性显著增强.
Cl-浓度
温度
钝化膜
Stainless steel 304
Cl- concentration
Temperature
Passive film
Abstract
Corrosion behaviour of stainless steel 304 in the solutions with different concentrations of NaCl was investigated by immersion test,polarization curve and EIS measurements.The obvious concentration of NaCl resulting in pitting corrosion was 0.4%,and pitting corrosion was aggravated with the increase of Cl- concentration and temperature.The EIS results showed that the destruction of passive film was greater when concentration of NaCl was larger than 0.4%.
中图分类号 TG172 TG142.7
所属栏目 试验研究
基金项目
收稿日期 2006/9/14
修改稿日期 2006/10/20
网络出版日期
作者单位点击查看
引用该论文: GONG Li-hua,ZHANG Bo,JIANG Lin-lin. CORROSION BEHAVIOR OF STAINLESS STEEL 304 AS WATER SUPPLY MATERIAL IN WATER CONTAINING CHLORIDE[J]. Corrosion & Protection, 2007, 28(8): 400～402
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】徐建平,刘丰,赵兰.不锈钢管在给水工程中的应用[J].建材技术与应用,2005(1):32-34.
【2】杨武.金属的局部腐蚀[M].北京:化学工业出版社,1995:76-77.
【3】葛红花,周国定,吴文权.316不锈钢在模拟冷却水中的钝化模型[J].中国腐蚀与防护学报,2004,24(2):65-70.
【4】刘烈伟,胡倩,郭风.硫化氢对不锈钢表面钝化膜破坏的研究[J].中国腐蚀与防护学报,2002,22(1):22-26.
【2】杨武.金属的局部腐蚀[M].北京:化学工业出版社,1995:76-77.
【3】葛红花,周国定,吴文权.316不锈钢在模拟冷却水中的钝化模型[J].中国腐蚀与防护学报,2004,24(2):65-70.
【4】刘烈伟,胡倩,郭风.硫化氢对不锈钢表面钝化膜破坏的研究[J].中国腐蚀与防护学报,2002,22(1):22-26.
相关信息