AZ91D镁合金化学镀镍磷研究
A STUDY ON ELECTROLESS PLATING Ni-P ON SURFACE OF AZ91D MAGNESIUM ALLOY
摘 要
采用磷酸和氟化钾为前处理酸洗液配方，以碱式碳酸镍为主盐，研究了AZ91D镁合金表面直接化学镀镍-磷工艺.并应用金相截面法对该工艺的镀层沉积速度进行了检测分析；应用X射线衍射分析技术（XRD）、附带能谱仪的扫描电镜(SEM)、显微硬度测试仪以及划痕测试仪等对镀层的形貌结构、成分、硬度及结合力等作了检测与分析.该工艺所获得镀层不仅沉积速率稳定，而且表面良好、性能优良，具有很好的实际工业应用推广意义.
化学镀
Ni-P合金
镀速
AZ91D magnesium alloy
Electroless plating
Ni-P alloy
Deposit velocity
Abstract
A direct electroless Ni-P plating on AZ91D magnesium alloy was investigated,which used H3PO4+KF as acid pickling pretreatment and 2NiCO3·3Ni(OH)2·4H2O as the main salt.The deposit velocity of the plating was measured by metallographical section.The microstructure,composition,micro-hardness and binding force of the coating were measured by using XRD,SEM,micro-hardness test and scratch test.With the optimum formula and deposit velocity,good plating surface and performance were obtained.
中图分类号 TQ153.2
所属栏目 应用技术
基金项目
收稿日期 2006/11/30
修改稿日期 2007/6/7
网络出版日期
作者单位点击查看
引用该论文: ZHANG Dao-jun,SHAO Hong-hong,JIANG Xiao-yan. A STUDY ON ELECTROLESS PLATING Ni-P ON SURFACE OF AZ91D MAGNESIUM ALLOY[J]. Corrosion & Protection, 2007, 28(10): 532～533
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘新宽,向阳辉,胡文彬,等.镁合金化学镀液的长周期使用[J].中国有色金属学报,2003,13(4):1046-1050.
【2】饶乾阳,蒙继龙,徐建.镁合金化学镀镍-磷新工艺[J].新技术新工艺,2005,3:63-67.
【3】Xiang Y H,Hu W B,Liu X K,et al.Initial deposition mechanism of electroless nickel plating on magnesium alloys[J].Trans IMF,2001,79(1):30-32.
【4】边凤刚,李国禄,刘金海,等.镁合金表面处理发展现状[J].材料保护,2002,35(3):1-4.
【5】李瑛,余刚,刘跃龙,等.镁合金的表面处理及其发展趋势[J].表面技术,2003,32(2):1-5.
【6】闫洪,杜强,邓之福.化学镀镍基合金的组织结构和腐蚀性能[J].有色金属,2007,22(1):5-9.
【2】饶乾阳,蒙继龙,徐建.镁合金化学镀镍-磷新工艺[J].新技术新工艺,2005,3:63-67.
【3】Xiang Y H,Hu W B,Liu X K,et al.Initial deposition mechanism of electroless nickel plating on magnesium alloys[J].Trans IMF,2001,79(1):30-32.
【4】边凤刚,李国禄,刘金海,等.镁合金表面处理发展现状[J].材料保护,2002,35(3):1-4.
【5】李瑛,余刚,刘跃龙,等.镁合金的表面处理及其发展趋势[J].表面技术,2003,32(2):1-5.
【6】闫洪,杜强,邓之福.化学镀镍基合金的组织结构和腐蚀性能[J].有色金属,2007,22(1):5-9.
相关信息