中高温拉拔型磷化液及磷化工艺
PHOSPHATING SOLUTION AND TECHNOLOGY FOR DRAWING AT MIDDLING AND HIGH TEMPERATURES
摘 要
以锌、钙、镍、锰为主要成膜物质，硝酸盐为促进剂，有机酸为稳定剂，研制了一种中高温拉拔型磷化液.该磷化液不含亚硝酸根，磷化过程中无需添加调整剂、沉渣少、性能稳定，其磷化膜特点在于耐磨、耐压，具有可塑性，主要用于金属标准件加工的前处理.通过钙离子浓度对磷化膜影响的研究，考察了总酸度、游离酸度、磷化时间以及磷化温度对膜重的影响，并得出了较佳的磷化工艺.
拉拔型
中高温
钢铁
Phosphating
Drawing
Middling and high temperature
Steel
Abstract
A phosphating solution was developed for middling and high temperature drawing,which used Zn-Ca-Ni-Mn as main materials of phosphating film,nitrate as accelerant and organic acid as stabilization agent.It had no nitrite and regulative agent,less sedimentary residue and more stable capability.The effects of Ca2+ concentration on total acidity,dissociative acidity,time and tempareture of phosphating processing on phosphating film were studied.Optimal phosphating parameters were obtained.
中图分类号 TG174.4
所属栏目 应用技术
基金项目
收稿日期 2006/10/20
修改稿日期 2006/11/7
网络出版日期
作者单位点击查看
引用该论文: ZHANG Li-wei,TIAN Heng-shui,ZHU Yun-feng. PHOSPHATING SOLUTION AND TECHNOLOGY FOR DRAWING AT MIDDLING AND HIGH TEMPERATURES[J]. Corrosion & Protection, 2007, 28(10): 540～542
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】韩恩山,王焕志.新型磷化液的研制[J].电镀与涂饰,2006,25(3):13-16.
【2】唐林,郑岷,张涛.高耐腐蚀锌钙系中温磷化液的研制[J].材料保护,2003,36(8).
【3】雷霆,李淑英.高耐蚀性中高温磷化液的研究[J].材料与表面处理技术,2006(1):108-110.
【4】郭良生,黄霓裳.sL-6B型常温锌系磷化液的研制[J].表面技术,1997,21(7):17-18.
【5】向鸿照,陈伟,陈天朗.Zn-Mn-Ca-Ni系中温磷化液的研究[J].材料保护,2004,37(5):13-16.
【6】胡煜艳,周承璋,徐蔚.锌钙系磷化液的研究[J].电镀与环保,2005,25(3):25-27.
【2】唐林,郑岷,张涛.高耐腐蚀锌钙系中温磷化液的研制[J].材料保护,2003,36(8).
【3】雷霆,李淑英.高耐蚀性中高温磷化液的研究[J].材料与表面处理技术,2006(1):108-110.
【4】郭良生,黄霓裳.sL-6B型常温锌系磷化液的研制[J].表面技术,1997,21(7):17-18.
【5】向鸿照,陈伟,陈天朗.Zn-Mn-Ca-Ni系中温磷化液的研究[J].材料保护,2004,37(5):13-16.
【6】胡煜艳,周承璋,徐蔚.锌钙系磷化液的研究[J].电镀与环保,2005,25(3):25-27.
相关信息