轴向应力对35CrMoA螺栓湿H2S应力腐蚀断裂的影响
INFLUENCE OF AXIAL STRESS ON SCC OF BOLTS IN WET H2S ENVIRONMENT
摘 要
采用自行设计的一套装置研究了螺栓(35CrMoA)在湿H2S环境中的失效过程,对螺栓的化学成分、微观组织、宏微观断口形貌及裂纹尖端应力情况进行了分析.试验和分析的结果表明,在湿H2S环境中35CrMoA螺栓在一定的应力水平下会发生应力腐蚀破坏.
35CrMoA钢
轴向应力
硫化氢
应力腐蚀开裂(SCC)
Bolt
35CrMoA steel
Axial stress
Hydrogen sulfide
Stress corrosion cracking(SCC)
Abstract
The failure of bolts made of 35CrMoA steel was studied by a self designed experimental approach.The analysis of component,microstructure fracture morphology of 35CrMoA steel and stress concentration at crack tip had been finished.The stress corrosion cracking would occur if the stress of the bolts made of 35CrMoA steel used in wet H2S environment is greater than a certain value.
中图分类号 TG172.8 TG172.9
所属栏目 试验研究
基金项目
收稿日期 2006/12/22
修改稿日期 2007/3/12
网络出版日期
作者单位点击查看
引用该论文: HE Jia-sheng,CUI Hao-xuan,ZHU Xiao-ming,LU Yuan-ming,WU Jian-ping,ZHU Guang-qiang. INFLUENCE OF AXIAL STRESS ON SCC OF BOLTS IN WET H2S ENVIRONMENT[J]. Corrosion & Protection, 2007, 28(11): 559～561
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】任凌波,任晓雷.压力容器腐蚀与控制[M].北京:化学工业出版设,2003:218.
【2】邹英杰,谢孔波,何文真,等.酸性水气提装置换热器小浮头螺栓断裂事故的分析[J].腐蚀与防护,2003,24(9):406-408.
【3】金杰,韩良洁,柳鲁典,等.浮头式热交换器管板紧固螺栓应力腐蚀失效分析[J].腐蚀与防护,1997,24(9):29-30.
【4】夏翔鸣,翟 羽,朱瑞松,等.螺栓在H2S介质中的断裂失效原因分析[J].压力容器,2001,18(4):56-58.
【5】何家胜,陈银强.螺栓光杆部位表面裂纹应力集中有限元分析[J].化工装备技术,2006,27(2):65-67.
【2】邹英杰,谢孔波,何文真,等.酸性水气提装置换热器小浮头螺栓断裂事故的分析[J].腐蚀与防护,2003,24(9):406-408.
【3】金杰,韩良洁,柳鲁典,等.浮头式热交换器管板紧固螺栓应力腐蚀失效分析[J].腐蚀与防护,1997,24(9):29-30.
【4】夏翔鸣,翟 羽,朱瑞松,等.螺栓在H2S介质中的断裂失效原因分析[J].压力容器,2001,18(4):56-58.
【5】何家胜,陈银强.螺栓光杆部位表面裂纹应力集中有限元分析[J].化工装备技术,2006,27(2):65-67.
相关信息