Preparation and Characterization of Organic-Inorganic Hybrid Nanofilms with Colloidal Silica
摘 要
采用溶胶-凝胶法,以甲基三乙氧基硅烷(MTEOS)和正硅酸乙酯 (TEOS)为原料,制备有机-无机杂化薄膜,又采用纳米硅溶胶对有机-无机杂化薄膜进行改性.硅溶胶改性后有机-无机杂化纳米薄膜透明而且光滑,大大提高了薄膜的临界厚度.以热失重(DTA/TG)、傅立叶红外光谱(FTIR)手段研究了薄膜材料的结构及性能随温度的变化,并对涂覆于不锈钢表面上的硅溶胶改性后有机-无机杂化薄膜的防腐蚀性能进行了实验检测.结果表明,硅溶胶改性后有机-无机杂化薄膜的热稳定性能明显提高,并具有优良的抗腐蚀性能.
Abstract
Organic-inorganic hybrid films were prepared by sol-gel process,using methyltriethoxysilane(MTEOS) and tetraethoxysilane(TEOS) as precursors.With the addition of colloidal silica nanoparticles,the preparation and characterization of the hybrid films were improved.The prepared hybrid nanofilms were dense,uniform and defect-free.The critical thickness of the hybrid nanofilms was increased with the addition of the colloidal silica.The relationship between structure and temperature was investigated by DTA/TG and FTIR.The corrosion resistance performance of the hybrid nanofilms applied on stainless steel was tested.The nanofilms showed high heat stability and excellent corrosion resistant properties.So the new nanofilms can provide long-term and environmentally corrosion protection.
中图分类号 TG178
所属栏目 试验研究
基金项目 安徽师范大学校青年基金项目(No 2007xqn69)
收稿日期 2007/1/22
修改稿日期 2007/6/15
网络出版日期
作者单位点击查看
引用该论文: WANG Xiu-hua,SUN Hong-xia,LIU Shou-hua. Preparation and Characterization of Organic-Inorganic Hybrid Nanofilms with Colloidal Silica[J]. Corrosion & Protection, 2008, 29(1): 25~27
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Zaharescu,Jitianu1 A,Brǎileanu1 A,et al.Composition and thermal stability of SiO2-based hybrid materials teos-mteos system[J].Journal of Thermal Analysis and Calorimetry,2003,71(4):421-428.
【2】Que Wenxiu,Hua X.Sol-Gel Derived Titania/γ-Glycidoxypropyltrimethoxysilane and Methyltrimethoxysilane Hybrid Materials for Optical Waveguides[J].Journal of Sol-Gel Science and Technology,2003,28(3)319-325.
【3】Que Wenxiu,Hua X,Zhang Q Y.Preparation and optical properties of patternable TiO2/ormosils hybrid films for photonics applications[J].Chemical Physics Letters,2003,369(4):354-360.
【4】Khramov A N,Balbyshev V N,Voevodin N N,et al.Nanostructured sol-gel derived conversion coatings based on epoxy-and amino-silanes[J].Progress in Organic Coatings,2003,47(2):207-213.
【5】Gallardo J,Galliano P.Thermal Evolution of Hybrid Sol-Gel Silica Coatings:A Structural Analysis,Journal of Sol-Gel Science and technology[J].2000,19(3):393-397.
【6】Maia S,Goncalves M,Almeida M.Densification of hybrid silica-titania sol-gel films studied by ellipsometry and FTIR[J].Mater,Sci Eng B,2000,76(2):193-199.
【7】Pellice S,Pablo Galliano.Hybrid Sol-Gel Coatings Produced from TEOS and γ-MPS[J].Journal of Sol-Gel Science and Technology,2003,28(1):81-86.
【2】Que Wenxiu,Hua X.Sol-Gel Derived Titania/γ-Glycidoxypropyltrimethoxysilane and Methyltrimethoxysilane Hybrid Materials for Optical Waveguides[J].Journal of Sol-Gel Science and Technology,2003,28(3)319-325.
【3】Que Wenxiu,Hua X,Zhang Q Y.Preparation and optical properties of patternable TiO2/ormosils hybrid films for photonics applications[J].Chemical Physics Letters,2003,369(4):354-360.
【4】Khramov A N,Balbyshev V N,Voevodin N N,et al.Nanostructured sol-gel derived conversion coatings based on epoxy-and amino-silanes[J].Progress in Organic Coatings,2003,47(2):207-213.
【5】Gallardo J,Galliano P.Thermal Evolution of Hybrid Sol-Gel Silica Coatings:A Structural Analysis,Journal of Sol-Gel Science and technology[J].2000,19(3):393-397.
【6】Maia S,Goncalves M,Almeida M.Densification of hybrid silica-titania sol-gel films studied by ellipsometry and FTIR[J].Mater,Sci Eng B,2000,76(2):193-199.
【7】Pellice S,Pablo Galliano.Hybrid Sol-Gel Coatings Produced from TEOS and γ-MPS[J].Journal of Sol-Gel Science and Technology,2003,28(1):81-86.
相关信息