钢材表面硅烷处理后的防蚀性能
Corrosion Resistance of Steels after Silane Coupling Agent Treatment
摘 要
采用硫酸铜点滴、线性极化、电化学阻抗等试验,对比研究了经硅烷偶联剂(SCA)和铬酸盐表面处理后的冷轧板的耐蚀性.结果表明经硅烷偶联剂表面处理后不但提高了基材的耐蚀性能,还提高了基材与涂层结合力,起到和铬酸盐钝化相同的防护效果.该方法有望取代造成环境污染的铬酸盐钝化工艺.
硅烷偶联剂
铬酸盐
电化学阻抗
线性极化
corrosion resistance
silane coupling agent(SCA)
chromate
EIS
linear polarization
Abstract
The corrosion-resistance of the cold rolled steels treated with silane coupling agent(SCA)and chromate was studied by the tests of CuSO4 dropping,linear polarization and EIS etc.The results showed that the corrosion resistance of the steels and the adhesion between the steel and the coating were enhanced by the SCA surface treatment.The corrosion protection performance of silane treatment is comparable to that of chromate treatment,The conventional chromate could be replaced by the SCA treatment.
中图分类号 TG178
所属栏目 试验研究
基金项目 海军工程大学基金资助项目(E308)
收稿日期 2007/3/28
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: CHEN Shan,CHEN Ren-lin,CHEN Xue-qun,LI Guo-ming. Corrosion Resistance of Steels after Silane Coupling Agent Treatment[J]. Corrosion & Protection, 2008, 29(4): 175～177
被引情况:
【1】刘贵昌,苏本泽,王立达,秦小勇,徐辉, "混凝土表面硅烷改性后的防腐蚀性能",腐蚀与防护 33, 1087-1090(2012)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杨俊华,肖旭.国外有机硅的发展动向[J].化工新型材料,1997(7):6-9.
【2】Danqing Zhu,W J van Ooij.Corrosion protection of metals by water-based silane mixtures of bis-[trimethoxysilylpropyl] amine and vinyltriacetoxysilane[J].Progress in Organic Coatings,2004(49):42-53.
【3】徐溢,藤毅,徐铭熙.硅烷偶联剂应用现状及金属表面处理新应用[J].表面技术,2001,30(3):48-51.
【4】徐溢,王楠,张小凤,等.直接用作金属表面新型防护涂层额硅烷偶联剂水解效果分析[J].腐蚀与防护,2000,21(4):157-159.
【5】W J van Ooij,D Zhu. Effect of a mine functional group on corrosion rate of iron coated with films of organofunctional silanes[J].Corrosion 157,2001:413-420.
【6】王雪明,李爱菊,李国丽,等.硅烷偶联剂在防腐涂层金属预处理中的应用研究[J].材料科学与工程学报,2005,23(1):146-150.
【7】张明宗,管从胜,王威强.有机硅烷偶联剂在金属表面预处理中的应用[J].腐蚀科学与防护技术,2001,13(2):96-100.
【8】徐溢,王楠,徐铭熙.钢铁表面防腐硅烷膜表面涂层[J].重庆大学学报(自然科学版),2001,24(2):135-136.
【9】陆峰,W J van Ooij.铝合金表面硅烷处理后腐蚀性能的研究[J].材料工程,1998(8):18-20.
【2】Danqing Zhu,W J van Ooij.Corrosion protection of metals by water-based silane mixtures of bis-[trimethoxysilylpropyl] amine and vinyltriacetoxysilane[J].Progress in Organic Coatings,2004(49):42-53.
【3】徐溢,藤毅,徐铭熙.硅烷偶联剂应用现状及金属表面处理新应用[J].表面技术,2001,30(3):48-51.
【4】徐溢,王楠,张小凤,等.直接用作金属表面新型防护涂层额硅烷偶联剂水解效果分析[J].腐蚀与防护,2000,21(4):157-159.
【5】W J van Ooij,D Zhu. Effect of a mine functional group on corrosion rate of iron coated with films of organofunctional silanes[J].Corrosion 157,2001:413-420.
【6】王雪明,李爱菊,李国丽,等.硅烷偶联剂在防腐涂层金属预处理中的应用研究[J].材料科学与工程学报,2005,23(1):146-150.
【7】张明宗,管从胜,王威强.有机硅烷偶联剂在金属表面预处理中的应用[J].腐蚀科学与防护技术,2001,13(2):96-100.
【8】徐溢,王楠,徐铭熙.钢铁表面防腐硅烷膜表面涂层[J].重庆大学学报(自然科学版),2001,24(2):135-136.
【9】陆峰,W J van Ooij.铝合金表面硅烷处理后腐蚀性能的研究[J].材料工程,1998(8):18-20.
相关信息