铝合金稀土磷化与铬磷化比较
Comparison of Rare Earth Phosphating and Chromate Phosphating on Aluminum Alloy
摘 要
采用电化学测试、全浸腐蚀试验和结合力测试,研究了6061铝合金铬磷化处理和以稀土为添加剂的磷酸盐处理所形成的化学转化膜的工艺性能.动力学研究表明,两者的成膜过程是不相同的.极化曲线测试结果显示,在弱极化区范围内,两者抗蚀性能相近,而在强极化区,铬磷化转化膜的抗蚀性优于以稀土为添加剂的磷酸盐化学处理所形成的转化膜,全浸腐蚀试验有类似的结果.结合力测试结果则表明,以稀土为添加剂的磷酸盐化学处理所形成的转化膜与有机涂层间的结合力要优于铬磷化转化膜.
磷化
耐蚀性
结合力
aluminum alloy
phosphating
corrosion resistance
adhension
Abstract
The performance of the chemical conversion coatings formed on 6061-aluminum alloy with chromate phosphate process and phosphate process with rare earth as additive was studied by electrochemical measurement,immersing corrosion test and adhesion test.The results showed that the film forming processes were different.In the weak polarized scope,both of the corrosion resistance were close,but in the strong polarized scope,the corrosion resistance of the films formed by chromate phosphate process was better than that by phosphate process with rare earth as additive.Adhesion force between the conversion coating formed by phosphate process with rare earth as additive and the organic coating surpassed that of chromate phosphate process.
中图分类号 TG178
所属栏目 试验研究
基金项目 河南省科技攻关研究项目(0424240074);河南省自然科学研究项目(200510476009)
收稿日期 2007/4/17
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHANG Sheng-lin,Wang Shao-ling,ZHANG Xiao-lin. Comparison of Rare Earth Phosphating and Chromate Phosphating on Aluminum Alloy[J]. Corrosion & Protection, 2008, 29(4): 192～194
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Boeing Company.Corrosion prevention and control[M].Seattle:Boeing Company,1994.
【2】隆小庆,邵荣宽.2024铝合金化学转化膜与磷化底漆耐蚀性的研究[J].中国腐蚀与防护学报,2003,23(3):156-157.
【3】周谟银.腐蚀剂和氧化剂对硬铝(LYl2)磷化过程的影响[J].腐蚀与防护,1998,19(5):231-237.
【4】ASTMD1654-92 Standard test method for evaluation of painted or coated specimens subjected to corrosive environments[S].
【5】GB/T 9286-1998,色漆和清漆漆膜的划格试验[S].
【6】王成,江峰.LY12-Al合金铬磷化处理[J].腐蚀科学与防护技术,2002,14(2):82-85.
【7】汪泉发,黎 燕.铝及其合金化学转化膜技术[J].电镀与环保,1993,13(7):11-14.
【8】张允诚,胡如南,向荣.电镀手册上册[M].北京:国防工业出版社,1997:890-893.
【9】谭海林,潘肇基,李新立.Fe2+对电镀锌板磷化的影响[J].材料保护,2003,36(7):42-44.
【10】曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002:302-304.
【11】王成,于宝兴,江峰,等.酸度及NaNO3对钢铁常温磷化的影响[J].腐蚀科学与防护技术,2001,13(5):132-135.
【12】邝钜炽.锌系磷化的稀土促进剂成膜机理研究[J].稀土,2006,27(2):27-29.
【2】隆小庆,邵荣宽.2024铝合金化学转化膜与磷化底漆耐蚀性的研究[J].中国腐蚀与防护学报,2003,23(3):156-157.
【3】周谟银.腐蚀剂和氧化剂对硬铝(LYl2)磷化过程的影响[J].腐蚀与防护,1998,19(5):231-237.
【4】ASTMD1654-92 Standard test method for evaluation of painted or coated specimens subjected to corrosive environments[S].
【5】GB/T 9286-1998,色漆和清漆漆膜的划格试验[S].
【6】王成,江峰.LY12-Al合金铬磷化处理[J].腐蚀科学与防护技术,2002,14(2):82-85.
【7】汪泉发,黎 燕.铝及其合金化学转化膜技术[J].电镀与环保,1993,13(7):11-14.
【8】张允诚,胡如南,向荣.电镀手册上册[M].北京:国防工业出版社,1997:890-893.
【9】谭海林,潘肇基,李新立.Fe2+对电镀锌板磷化的影响[J].材料保护,2003,36(7):42-44.
【10】曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002:302-304.
【11】王成,于宝兴,江峰,等.酸度及NaNO3对钢铁常温磷化的影响[J].腐蚀科学与防护技术,2001,13(5):132-135.
【12】邝钜炽.锌系磷化的稀土促进剂成膜机理研究[J].稀土,2006,27(2):27-29.
相关信息