GCr15轴承钢穿管腐蚀问题分析及改进措施
Analysis and Improvement Measures of Corrosion Problems during Piercing of GCr15 Bearing Steel
摘 要
对GCr15轴承钢在穿管酸洗过程中出现的耗酸过多、过酸及氧化铁皮不易脱落等腐蚀问题进行了分析和试验,得出铜元素含量是影响其耐蚀性能的主要原因.在此基础上提出在转炉钢中添加少量的铜,取得了良好效果.
穿管
酸洗
腐蚀
措施
GCr15 bearing steel
piercing
pickling
corrosion
improvement measure
Abstract
The analyses and testing on the corrosion problems like too much acid consumption during pickling,over-pickling and difficult falling off of scales indicated that the main cause to influence the corrosion resistance during the piercing of GCr15 bearing steel was the copper content.Some improvement measures were put forward and good effects have been obtained.
中图分类号 TG172
所属栏目 应用技术
基金项目
收稿日期 2008/1/26
修改稿日期 2008/2/1
网络出版日期
作者单位点击查看
引用该论文: FAN Xi-pin,ZHANG Ying,PANG Chun-hu,WANG Ling-guo. Analysis and Improvement Measures of Corrosion Problems during Piercing of GCr15 Bearing Steel[J]. Corrosion & Protection, 2008, 29(7): 401～403
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】冶金工业部钢铁研究院主编.合金钢手册[M].北京:中国工业出版社,1971.153.
【2】马丽微,王向东,陈小平,等.铜对碳钢耐大气腐蚀的影响[J].天津冶金,2007(5):21.
【3】钢铁研究所岩相研究室.耐大气腐蚀锈层结构研究[J].武钢技术,1978(4):38.
【4】严谨,熊长清.含铜低合金钢耐大气腐蚀性能研究[J].中国腐蚀与防护学报,1986,6(1):1.
【2】马丽微,王向东,陈小平,等.铜对碳钢耐大气腐蚀的影响[J].天津冶金,2007(5):21.
【3】钢铁研究所岩相研究室.耐大气腐蚀锈层结构研究[J].武钢技术,1978(4):38.
【4】严谨,熊长清.含铜低合金钢耐大气腐蚀性能研究[J].中国腐蚀与防护学报,1986,6(1):1.
相关信息