Corrosion Behavior of Cu-Ni Alloy in 55%LiBr Solution with Different Inhibitor
摘 要
采用电化学阻抗技术研究了LiOH、Na2MoO4和BTA对铜镍合金在55%LiBr溶液中的腐蚀行为的影响.结果表明,单独添加LiOH和BTA都能显著减缓铜镍合金在LiBr溶液中的腐蚀,而Na2MoO4含量较低时可能会加速腐蚀.三种缓蚀剂复配使用,对铜镍合金在55%LiBr 溶液中的腐蚀具有更好的缓蚀效果,复配后具有协同效应.试验表明,复合添加0.10 mol/L LiOH、150 mg/L Na2MoO4和150 mg/L BTA时,对铜镍合金在55%LiBr溶液中的腐蚀具有最优的缓蚀效率.
Abstract
The effects of LiOH,Na2MoO4 and BTA on the corrosion behavior of Cu-Ni alloy in 55%LiBr solution was studied by EIS measurements.Results indicated that LiOH or BTA could decrease the corrosion rate of Cu-Ni alloy,but Na2MoO4 might increase the corrosion rate when its concentration was lower than a critical value.When LiOH,Na2MoO4 and BTA were used together,the inhibition efficiency on Cu-Ni alloy was higher than that when was used one of them.They behaved with a synergistic effect on inhibiting the corrosion of Cu-Ni alloy in 55%LiBr solution.When the concentration of LiOH,Na2MoO4 and BTA was 0.10 mol/L,150 mg/L and 150 mg/L,respectively,the inhibition efficiency on the corrosion of Cu-Ni alloy in 55%LiBr solution was optimal.
中图分类号 TG174.42
所属栏目 试验研究
基金项目
收稿日期 2007/7/3
修改稿日期 2008/3/25
网络出版日期
作者单位点击查看
引用该论文: HU Xian-qi,LIANG Cheng-hao. Corrosion Behavior of Cu-Ni Alloy in 55%LiBr Solution with Different Inhibitor[J]. Corrosion & Protection, 2008, 29(8): 448~450
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Felix Z.Recent developments and future prospects of sorption heat pump systems[J].International Journal of Thermal Sciences,1999,38(3):191-208.
【2】Felix Z.State of the art in sorption heat pumping and cooling technologies[J].International Journal of Refrigeration,2002,25(4):450-459.
【3】梁成浩,郭建伟.溴化锂吸收式制冷机中缓蚀剂的应用与发展[J].腐蚀与防护,2000,21(5):206-209.
【4】Igual-Muňoz A MT,Garcia-Anton J,Guiňón J L,et al.Corrosion studies of Cu-Ni alloys in aqueous LiBr solutions[C]//EUROCORR 2000,Queen Mary and Westfield College,University of London,London,2000:00040803.
【5】朱祖芳.有色金属的耐腐蚀性及其应用[M].北京:化学工业出版社,1994.
【6】梁成浩,扈显琦,毕程.铜在55%LiBr溶液中腐蚀行为的交流阻抗研究[J].中国腐蚀与防护学报,2006,26(sup.):34-37.
【2】Felix Z.State of the art in sorption heat pumping and cooling technologies[J].International Journal of Refrigeration,2002,25(4):450-459.
【3】梁成浩,郭建伟.溴化锂吸收式制冷机中缓蚀剂的应用与发展[J].腐蚀与防护,2000,21(5):206-209.
【4】Igual-Muňoz A MT,Garcia-Anton J,Guiňón J L,et al.Corrosion studies of Cu-Ni alloys in aqueous LiBr solutions[C]//EUROCORR 2000,Queen Mary and Westfield College,University of London,London,2000:00040803.
【5】朱祖芳.有色金属的耐腐蚀性及其应用[M].北京:化学工业出版社,1994.
【6】梁成浩,扈显琦,毕程.铜在55%LiBr溶液中腐蚀行为的交流阻抗研究[J].中国腐蚀与防护学报,2006,26(sup.):34-37.
相关信息