改性水性环氧树脂乳液对石质文物的保护效果
Preservation Effect of Modified Waterborne Epoxy Resin Emulsion for Stone Historical Relic
摘 要
通过添加硅酸盐对水性环氧树脂乳液进行改性,制备了石质文物表面防护剂.以山西大同云冈石窟的砂岩为保护对象,测定了该表面防护剂的防水性、耐水性、接触角、耐紫外线、安定性和耐盐性等性能指标.结果表明,硅酸盐改性水性环氧树脂乳液对石质文物的表面保护具有良好的效果.
水性环氧树脂乳液
石质文物保护
silicate
water-borne epoxy resin emulsion
stone
historical relic preservation
Abstract
Silicate was used to enhance the property of water-borne epoxy resin emulsion and a kind of surface repellent for stone historical relic was prepared.The main properties of the surface repellent,such as water resistance and salt resistance,freeze-thaw resistance and absorption to ultraviolet light,were improved in comparison with silicate free water-borne epoxy resin emulsion by using the sandstone in Shangxi Datong Yungang Grotto as a sample,It is excellent environmental paint for preservation of stone historical relic.
中图分类号 TU503
所属栏目 试验研究
基金项目
收稿日期 2007/8/2
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: LUAN Xiao-xia,XU Chun-chun,WANG Zi-se,JI Jing. Preservation Effect of Modified Waterborne Epoxy Resin Emulsion for Stone Historical Relic[J]. Corrosion & Protection, 2008, 29(8): 451～453
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张秉坚,铁景沪.石质古迹的防护材料及存在的问题[J].石材,1999(12):5-7.
【2】P Laurie A P,Rankin C.Journal of the society of the chemical industry[J].1978(37):137-147.
【3】周继亮.室温固化柔韧性水性环氧固化剂的合成与性能[J].高分子材料科学与工程,2006(1):53-55.
【4】杨振忠,许元泽,徐懋.环氧树脂水基化微粒化体系[J].高分子通报,1997(9):190.
【5】顾国芳,陈铤,陶俊.Ⅱ型水性环氧树脂涂料特性研究[J].化学建材,2001,17(3):16-20.
【6】刘国杰.现代涂料工艺新技术[M].北京:中国轻工业出版社,2000:65.
【2】P Laurie A P,Rankin C.Journal of the society of the chemical industry[J].1978(37):137-147.
【3】周继亮.室温固化柔韧性水性环氧固化剂的合成与性能[J].高分子材料科学与工程,2006(1):53-55.
【4】杨振忠,许元泽,徐懋.环氧树脂水基化微粒化体系[J].高分子通报,1997(9):190.
【5】顾国芳,陈铤,陶俊.Ⅱ型水性环氧树脂涂料特性研究[J].化学建材,2001,17(3):16-20.
【6】刘国杰.现代涂料工艺新技术[M].北京:中国轻工业出版社,2000:65.
相关信息