某厂尿素合成塔层板开裂事故分析
Analyses of Cracking Accident of Laminated Plate in A Carbamide Synthetic Tower
摘 要
某厂尿素合成塔内衬里完好,但层板及焊缝多处开裂.分析结果认为,该合成塔产生大量应力腐蚀裂纹的原因在于使用二次蒸汽检漏,且检漏口密封不严,导致二次蒸汽漏入层板之间,同时该合成塔存在较大拉应力.对此提出了改用空气检漏等若干建议.
层板
开裂
carbamide synthetic tower
laminated plate
cracking
Abstract
The lining of a carbamide synthetic tower was in good condition.But there were a lot of cracks in many laminated plates and welding lines.The reason for cracking was analyzed.The leaking of discharge steam used for leakage detection into the laminated plates and the existance of great tensile stress in the tower resulted in stress corrosion cracking.Some proposals such as using the air to detect leakage etc are suggested.
中图分类号 TG172.9
所属栏目 失效分析
基金项目 国家自然科学基金(29966001);广西自然科学基金(桂科青0447005);广西大学自然科学基金项目资助
收稿日期 2007/9/5
修改稿日期 2007/10/9
网络出版日期
作者单位点击查看
引用该论文: Lin Jing-yu,Lin Qing-yu,Lin Rong-duan,Zhou Jian-xing,Zhang Gui-you. Analyses of Cracking Accident of Laminated Plate in A Carbamide Synthetic Tower[J]. Corrosion & Protection, 2008, 29(9): 566～568
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】池树增.国外某厂尿素合成塔爆破事故原因初探[J].中氮肥,2006(2):10-13,47.
【2】济南市人民政府鲁西化工第三化肥厂有限公司“3.21”尿素合成塔爆炸事故调查组.“3.21”尿素合成塔爆炸事故调查报告[R].中国化工报,2006-6-17(007版).
【3】国家质检局.关于进一步加强尿素合成塔使用检验工作的通知[J].化工标准计量质量,2005,25(11):3-4.
【4】龚斌.压力容器破裂的防治[M].杭州:浙江科技出版社,1985.
【5】GB 150-1998,钢制压力容器[S].
【6】GB/T 19624-2004,在用含缺陷压力容器安全评定[S].
【7】郑津洋.过程设备设计[M].北京:化工出版社,2005:46.
【2】济南市人民政府鲁西化工第三化肥厂有限公司“3.21”尿素合成塔爆炸事故调查组.“3.21”尿素合成塔爆炸事故调查报告[R].中国化工报,2006-6-17(007版).
【3】国家质检局.关于进一步加强尿素合成塔使用检验工作的通知[J].化工标准计量质量,2005,25(11):3-4.
【4】龚斌.压力容器破裂的防治[M].杭州:浙江科技出版社,1985.
【5】GB 150-1998,钢制压力容器[S].
【6】GB/T 19624-2004,在用含缺陷压力容器安全评定[S].
【7】郑津洋.过程设备设计[M].北京:化工出版社,2005:46.
相关信息