透明陶瓷镁铝尖晶石MgAl2O4耐酸碱性能的初步研究
Corrosion-resistance of Transparent Ceramic Spinel MgAl2O4
摘 要
对透明陶瓷MgAl2O4在不同浓度和不同温度条件下的耐酸碱性能进行了初步研究.结果表明,在常温和75 ℃条件下,透明陶瓷MgAl2O4对不同浓度的盐酸溶液、磷酸溶液和氢氧化钠溶液具有较好的耐酸、耐碱性；在温度高于300 ℃时,对浓H3PO4具有较弱的耐酸性,对熔融的NaOH有一定的耐碱性.
镁铝尖晶石
腐蚀
耐酸碱性
transparent ceramic
MgAl2O4
corrosion
corrosion resistance
Abstract
The corrosion-resistance of transparent ceramic MgAl2O4 was studied under the conditions of different concentrations and temperatures.The results indicated that transparent ceramic MgAl2O4 had relatively good corrosion resistance in hydrochloric acid,phosphoric acid and sodium hydroxide with different concentrations at normal temperature and 75 ℃.The corrosion resistance of transparent ceramic MgAl2O4 in concentrated phosphoric acid was bad at temperatures higher than 300 ℃ but good in fused sodium hydroxide.
中图分类号 TB321
所属栏目 试验研究
基金项目
收稿日期 2007/12/21
修改稿日期 2008/1/10
网络出版日期
作者单位点击查看
引用该论文: WEN Fang,HE Ting-qiu,LEI Mu-yun,SONG Qing-hai,HUANG Cun-xin. Corrosion-resistance of Transparent Ceramic Spinel MgAl2O4[J]. Corrosion & Protection, 2009, 30(1): 36～38
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】闻芳,杜洪兵,雷牧云,等.铝尖晶石超细粉末的制备[J].现代技术陶瓷,2003(3):3-6.
【2】刘道新.材料的腐蚀与防护[M].西安:西北工业大学出版社,2006.
【3】顾少轩,赵修建,胡军.陶瓷的腐蚀行为和腐蚀机理研究进展[J].材料导报,2006,16(6):42-44.
【4】朱立群.陶瓷材料的腐蚀[J].兵器材料科学与工程,1995,18(4):50-53.
【5】麦考利.陶瓷腐蚀[M].高南,张启富,顾宝珊,译.北京:冶金工业出版社,2003.
【2】刘道新.材料的腐蚀与防护[M].西安:西北工业大学出版社,2006.
【3】顾少轩,赵修建,胡军.陶瓷的腐蚀行为和腐蚀机理研究进展[J].材料导报,2006,16(6):42-44.
【4】朱立群.陶瓷材料的腐蚀[J].兵器材料科学与工程,1995,18(4):50-53.
【5】麦考利.陶瓷腐蚀[M].高南,张启富,顾宝珊,译.北京:冶金工业出版社,2003.
相关信息