钢铁表面水性透明耐蚀涂层的研制
Preparation and Properties of Waterborne Corrosion Resistant Transparent Coating on Steel
摘 要
以苯丙乳液为主要成膜物质,利用正交试验优化各助剂用量得到了涂料的最佳配方,制备了适用于钢铁表面的水性透明耐蚀涂层.试验结果表明:该涂层具有良好的附着力、耐蚀性、耐湿热性、抗老化性、柔韧性、耐冲击性、透光性和回粘性,而且该涂料的最低成膜温度为4.9 ℃,可以满足钢铁在室外的防护要求.
透明
耐蚀性
waterborne coating
transparency
corrosion resistance
Abstract
Using various auxiliaries,taking styrene-acrylic as principal film-former,the optimum formula had been obtained by orthogonal design and a kind of waterborne transparent corrosion resistant coating adaptable to the surface of steel has been prepared.The results indicated that this coating had better feature of adhesion as well as tarnish resistance,humidity resistance,withering resistance,flexibility,impact resistance and temperature change resistance.Moreover,the lowest temperature of film-formation reached 4.9 ℃.The coating can meet the protection requirement of steel outdoors.
中图分类号 TG174.2
所属栏目 应用技术
基金项目
收稿日期 2007/11/6
修改稿日期 2007/11/12
网络出版日期
作者单位点击查看
引用该论文: ZHANG Jing,QIAN Jian-gang,TIAN Pei-qiu,DAI Chun-li. Preparation and Properties of Waterborne Corrosion Resistant Transparent Coating on Steel[J]. Corrosion & Protection, 2009, 30(1): 59～61
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】夏赤丹,周福香,肖莹.水性涂料工业的进展[J].江汉大学学报(自然科学版).2004(3):30-33.
【2】涂伟萍.水性涂料[M].北京:化学工业出版社,2006:36.
【3】马庆麟.涂料工业手册[M].北京:化学工业出版社,2006:467.
【4】耿星.现代水性涂料助剂手册[M].北京:中国石化出版社,2007:206-211.
【5】钱逢麟,竺玉书.涂装助剂[M].北京:化学工业出版社,1990:150.
【2】涂伟萍.水性涂料[M].北京:化学工业出版社,2006:36.
【3】马庆麟.涂料工业手册[M].北京:化学工业出版社,2006:467.
【4】耿星.现代水性涂料助剂手册[M].北京:中国石化出版社,2007:206-211.
【5】钱逢麟,竺玉书.涂装助剂[M].北京:化学工业出版社,1990:150.
相关信息