提高管道外防腐层施工质量的途径
The Way to Improve External Pipeline Coating Quality
摘 要
已广泛应用的三层聚烯烃结构防腐层(3LPO)和单层熔结环氧粉末涂层(FBE)已相继发生了多起投产运营三五年后防腐层粘结性下降并完全失效的事故.为减少此类事故的发生,提出了通过提高表面处理质量和优化环氧粉末涂敷工艺来改进管道外防腐层施工质量的途径,并通过实例进行了效果验证.结果表明,上述措施改进效果明显,可推广使用.
单层熔结环氧粉末涂层
表面质量
涂敷工艺
three layer polyolefin coating(3LPO)
fusion bonded epoxy(FBE)
surface quality
coating process
Abstract
Because of excellent anti-corrosion property,three layer polyolefin coatings(3LPO)and fusion bonded epoxy(FBE) have dominated the pipe coating market in the world.But poor adhesion has been identified on pipelines coated with 3LPO & FBE coatings in 3 or 5 years all over the world.To improve the pipeline coating quality,a new blasting technology and an optimum coating process have been introduced.The practical results indicate that they are very effective to improve 3LPE coating quality.
中图分类号 TG174.4
所属栏目 应用技术
基金项目
收稿日期 2007/12/8
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: CHANG Yong-yi,DOU Xue-zong. The Way to Improve External Pipeline Coating Quality[J]. Corrosion & Protection, 2009, 30(1): 64～65
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】David Norman.Pipeline coatings-the good the bad and the ugly［C］//Australian Corrosion Conference,2002.
【2】SY/T0413-2002.埋地钢质管道聚乙烯防腐层技术标准[S].北京:石油工业出版社,2002.
【3】Dale W Schadfer,Guirong Pan,Wim vanOoij.Anticorrosion coatings can they be made without chromium[J].Los Alamos Science,2006(30):172-177.
【4】李爱菊,王雪明,王威强,等.金属表面硅烷化预处理制备聚乙烯涂层的研究[J].腐蚀科学与防护技术,2007(2):126-130.
【5】许传新,种志伯,程书旗,等.三层聚乙烯外涂敷作业线生产速度的确定因素[J].防腐保温技术,2005(3):16-18.
【6】常永懿.用DSC法研究管道熔结环氧粉末涂料固化特性[J].焊管,2008(3):24-27.
【2】SY/T0413-2002.埋地钢质管道聚乙烯防腐层技术标准[S].北京:石油工业出版社,2002.
【3】Dale W Schadfer,Guirong Pan,Wim vanOoij.Anticorrosion coatings can they be made without chromium[J].Los Alamos Science,2006(30):172-177.
【4】李爱菊,王雪明,王威强,等.金属表面硅烷化预处理制备聚乙烯涂层的研究[J].腐蚀科学与防护技术,2007(2):126-130.
【5】许传新,种志伯,程书旗,等.三层聚乙烯外涂敷作业线生产速度的确定因素[J].防腐保温技术,2005(3):16-18.
【6】常永懿.用DSC法研究管道熔结环氧粉末涂料固化特性[J].焊管,2008(3):24-27.
相关信息