Stress Corrosion Cracking of X70 Steel with Different Microstructures in Acid Soil Simulation Solution
摘 要
采用慢应变速率拉伸试验(SSRT)及断口观测研究了不同显微组织X70钢的应力腐蚀破裂(SCC)敏感性.结果表明:X70钢及其不同热处理后的劣化组织在鹰潭土壤模拟溶液中均具有明显的SCC敏感性;三种组织X70钢的SCC敏感性整体上表现为随外加电位的降低而增大,组织硬化和晶粒过大都能增加材料的SCC敏感性.
Abstract
The stress corrosion cracking(SCC)susceptibility of X70 steel with three types of microstructure was analyzed by means of slow strain rate testing(SSRT)and fracture surface(SEM)observation.The experimental results illustrated that the steel after different heat treatments had higher SCC susceptibility than the as received steel.With decreasing polarization potential,the SCC susceptibility of the X70 with different kinds of microstructure increased.Both hardening and grain coarsening can increase the SCC susceptibility.
中图分类号 TG172.4
所属栏目 试验研究
基金项目 国家科技基础条件平台建设项目(2005DKA 10400);“十五”规划重大项目基金资助项目(50499333-08)
收稿日期 2008/1/14
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHAI Guo-li,LIU Zhi-yong,DU Cui-wei,LI Xiao-gang,WANG Li-xian. Stress Corrosion Cracking of X70 Steel with Different Microstructures in Acid Soil Simulation Solution[J]. Corrosion & Protection, 2009, 30(3): 149~152
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杨武.埋地油气管线应力腐蚀破裂研究的一些新进展[J].腐蚀与防护2003,11,24(11):461-467.
【2】方丙炎,王俭秋,朱自勇,等.埋地管道在近中性pH和高pH环境中地应力腐蚀开裂[J].金属学报,2001,37(5):454-458.
【3】Jack T R,Erno B,Krist K.Generation of near neutral pH and high pH SCC environments on buried pipelines[C]//Corrosion/2000.NACE International Houston,TX:2000:362.
【4】黄春波,李光福,杨武.X70管线钢焊缝应力腐蚀破裂的研究[J].腐蚀与防护,2005,26(1):1-3.
【5】Lee J S,Ju J B,Jang J.Fracture toughness anisotropy in a API steel line-pipe[J].Materials Letters,2007,61(29):5178-5180.
【6】许淳淳,池琳,胡钢,等.HCO-3浓度对X70钢阳极反应过程的影响[J].中国腐蚀与防护学报,2005,25(1):20-24.
【7】Chin D T,Sabde G M.Current distribution and electrochemical environment in a cathodically protected crevice[J].Corrosion,1999,55(3):229-235.
【8】Van Boven G,Chen W,Rogge R.The role of residual stress in neutral pH stress corrosion cracking of pipeline steels.Part I:Pitting and cracking occurrence[J].Acta Meterial,2006,2:1-3.
【9】李晓刚,杜翠薇,董超芳,等.X70钢的腐蚀行为与试验研究[M].北京:科学出版社,2006:13.
【10】Qiao L J,Luo J L,Mao X.Hydrogen evolution and enrichment around stress corrosion crack tips of pipeline steels in dilute bicarbonate solution[J].Corrosion,1998,54(2):115-120.
【11】Lee S k,Kim B c,Kwon D.Correlation of microstructure and fracture properties in weld heat affected zones of thermo-mechanic-alloy controlled proposed steels[J].Metal Transaction,1992,23A:2803-2809.
【12】于少飞,钱百年,国旭鸣.加速冷却对X70钢热影响区组织与韧性的影响[J].金属学报,2005,41(4):402-406.
【13】陈玉华,王勇,韩彬.X70钢在役焊接热循环及粗晶区组织性能研究[J].兵器材料科学与工程,2005,28(4):22-25.
【2】方丙炎,王俭秋,朱自勇,等.埋地管道在近中性pH和高pH环境中地应力腐蚀开裂[J].金属学报,2001,37(5):454-458.
【3】Jack T R,Erno B,Krist K.Generation of near neutral pH and high pH SCC environments on buried pipelines[C]//Corrosion/2000.NACE International Houston,TX:2000:362.
【4】黄春波,李光福,杨武.X70管线钢焊缝应力腐蚀破裂的研究[J].腐蚀与防护,2005,26(1):1-3.
【5】Lee J S,Ju J B,Jang J.Fracture toughness anisotropy in a API steel line-pipe[J].Materials Letters,2007,61(29):5178-5180.
【6】许淳淳,池琳,胡钢,等.HCO-3浓度对X70钢阳极反应过程的影响[J].中国腐蚀与防护学报,2005,25(1):20-24.
【7】Chin D T,Sabde G M.Current distribution and electrochemical environment in a cathodically protected crevice[J].Corrosion,1999,55(3):229-235.
【8】Van Boven G,Chen W,Rogge R.The role of residual stress in neutral pH stress corrosion cracking of pipeline steels.Part I:Pitting and cracking occurrence[J].Acta Meterial,2006,2:1-3.
【9】李晓刚,杜翠薇,董超芳,等.X70钢的腐蚀行为与试验研究[M].北京:科学出版社,2006:13.
【10】Qiao L J,Luo J L,Mao X.Hydrogen evolution and enrichment around stress corrosion crack tips of pipeline steels in dilute bicarbonate solution[J].Corrosion,1998,54(2):115-120.
【11】Lee S k,Kim B c,Kwon D.Correlation of microstructure and fracture properties in weld heat affected zones of thermo-mechanic-alloy controlled proposed steels[J].Metal Transaction,1992,23A:2803-2809.
【12】于少飞,钱百年,国旭鸣.加速冷却对X70钢热影响区组织与韧性的影响[J].金属学报,2005,41(4):402-406.
【13】陈玉华,王勇,韩彬.X70钢在役焊接热循环及粗晶区组织性能研究[J].兵器材料科学与工程,2005,28(4):22-25.
相关信息