聚氯乙烯树脂溶剂型可剥性塑料的配方及性能
A Separable Plastic of Solvent Polyvinyl Chloride Resin
摘 要
采用对比试验的方法,研制出一种聚氯乙烯树脂溶剂型可剥性塑料;分别在3.5% NaCl、5% H2SO4、10% NaOH溶液中进行了耐蚀性试验,并测试了耐湿热性能和抗盐雾性能.结果表明:研制的可剥性塑料具有较好的耐酸碱盐、耐盐雾等性能和优良的柔韧性和抗冲击强度;该产品膜层光亮、流平性好、易于施涂、启封方便.
聚氯乙烯
缓蚀剂
separable plastic
polyvinyl chloride
corrosion inhibitor
Abstract
A separable plastic of solvent polyvinyl chloride resin was developed.Humid heat test,salt spray test,and corrosion tests in 3.5% NaCl,5% H2SO4 and 10% NaOH solutions were conducted to evaluate its corrosion resistance and mechanical properties.The results indicated that the separable plastic had superior corrosion resistance in acid,alkali,salt solution and salt spray environment.The plastic presented a bright film,with good levelling property etc.
中图分类号 TG174.46
所属栏目 试验研究
基金项目
收稿日期 2008/3/17
修改稿日期 2008/4/17
网络出版日期
作者单位点击查看
引用该论文: WANG Xing-fei,LIANG Cheng-hao,HUANG Nai-bao. A Separable Plastic of Solvent Polyvinyl Chloride Resin[J]. Corrosion & Protection, 2009, 30(3): 184～185
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赖光直一.可剥性塑料[J].防锈管理,1968,10(12):458-460.
【2】闫建忠,梁成浩.乙基纤维素基溶剂型可剥性塑料[J].材料保护,1998,31(4):29-31.
【3】姚淑霞.聚苯乙烯树脂溶剂型可剥防锈塑料的研制[J].中国环境管理干部学院学报,2001,14(1):26-27.
【4】乔冬平,谭瑛.可剥性塑料的研制[J].化学推进剂与高分子材料,1999(5):27-29.
【5】高群,王国建,郭岚.热塑性树脂在机床刀具表面防锈上的应用[J].材料保护,2002,35(2):52-53.
【6】王文广.塑料配方设计[M].北京:化学工业出版社,2004:50.
【2】闫建忠,梁成浩.乙基纤维素基溶剂型可剥性塑料[J].材料保护,1998,31(4):29-31.
【3】姚淑霞.聚苯乙烯树脂溶剂型可剥防锈塑料的研制[J].中国环境管理干部学院学报,2001,14(1):26-27.
【4】乔冬平,谭瑛.可剥性塑料的研制[J].化学推进剂与高分子材料,1999(5):27-29.
【5】高群,王国建,郭岚.热塑性树脂在机床刀具表面防锈上的应用[J].材料保护,2002,35(2):52-53.
【6】王文广.塑料配方设计[M].北京:化学工业出版社,2004:50.
相关信息