高Cl-条件下H2S分压对P110钢腐蚀速率的影响
Effect of H2S Partial Preesure on Corrosion Rate of P110 Steel under High Cl- Oil Condition
摘 要
利用高温高压釜设备模拟油气田环境并辅以失重法,研究了高Cl-条件下H2S分压对P110钢腐蚀速率的影响,结果表明:P110钢的腐蚀速率随着H2S分压的增大呈先增大后减小的趋势,且在0.06 MPa时取得最大值;采用扫描电子显微镜(SEM)、X射线衍射(XRD)和X射线能谱仪(EDS)技术对腐蚀产物膜进行分析知:H2S分压通过影响腐蚀产物膜厚度、微观吸附形貌和表面膜成分等,进而影响了P110钢的腐蚀速率.
H2S分压
Cl-
腐蚀速率
P110 steel
H2S partial preesure
Cl-
corrosion rate
Abstract
Effect of H2S partial pressure on corrosion rate of P110 steel under high Cl- condition was investigated in the autoclave containing stimulating oil and gas field environment,and the corrosion rate was measured by the weight loss method.And the corrosion scales were analyzed using SEM,XRD and EDS,The results showed that the corrosion rate of P110 steel increased first and decreased subsequently with the increase of H2S partial pressure,and the maximal corrosion rate was presented at 0.06 MPa.H2S partial pressure affected of and thus influenced the corrosion rate the thickness,surface morphology,composition of the corrosion scale of P110 steel and thus influenced the corrosion rate.
中图分类号 TG172.8
所属栏目 试验研究
基金项目 中国石油天然气集团公司应用基础研究资助项目(06A40302)
收稿日期 2008/4/30
修改稿日期 2008/7/14
网络出版日期
作者单位点击查看
引用该论文: ZHU Shi-dong,BAI Zhen-quan,LIN Guan-fa,YIN Cheng-xian,LIU Hui. Effect of H2S Partial Preesure on Corrosion Rate of P110 Steel under High Cl- Oil Condition[J]. Corrosion & Protection, 2009, 30(5): 293～296
被引情况:
【1】李谦定,卢永斌,李善建,卞雯,刘永毅,张菅,秦倩倩, "P110钢盐酸酸化缓蚀剂QL-1的合成及应用性能",腐蚀与防护 33, 289-292(2012)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】LyerR N,Takeuchi I.Hydrogen sulfide effect on hydrogen entry into iron[J].Corrosion,1990,46(7):415-418.
【2】Nesic S,Lunde L.Carbon dioxide corrosion ofcarbon steel in two-phase flow[J].Corrosion,1994,50(9):717-720.
【3】戴金星,胡见义,贾承造,等.科学安全勘探开发高含硫化氢天然气田的建议[J].石油勘探与开发,2004,31(2):1-4.
【4】朱世东,白真权,刘 会,等.影响油气田CO2腐蚀速率的因素研究[J].内蒙古石油化工,2008(5):6-10.
【5】白真权,李鹤林,刘道新,等.模拟油田H2S/CO2环境中N80钢的腐蚀及影响因素研究[J].材料保护,2003,36(4):32-34.
【6】李建平,赵国仙.高矿化度油田水中P110油管钢[J].材料与冶金学报,2003,3(1):54-57.
【7】张学元,邸超,雷良才.二氧化碳腐蚀与控制[M].北京:化学工业出版社,2000:57.
【2】Nesic S,Lunde L.Carbon dioxide corrosion ofcarbon steel in two-phase flow[J].Corrosion,1994,50(9):717-720.
【3】戴金星,胡见义,贾承造,等.科学安全勘探开发高含硫化氢天然气田的建议[J].石油勘探与开发,2004,31(2):1-4.
【4】朱世东,白真权,刘 会,等.影响油气田CO2腐蚀速率的因素研究[J].内蒙古石油化工,2008(5):6-10.
【5】白真权,李鹤林,刘道新,等.模拟油田H2S/CO2环境中N80钢的腐蚀及影响因素研究[J].材料保护,2003,36(4):32-34.
【6】李建平,赵国仙.高矿化度油田水中P110油管钢[J].材料与冶金学报,2003,3(1):54-57.
【7】张学元,邸超,雷良才.二氧化碳腐蚀与控制[M].北京:化学工业出版社,2000:57.
相关信息