热处理对A3钢在NaHCO3溶液中耐蚀性能的影响
Effect of Heat Treatment on Corrosion Resistance of A3 Steel in Sodium Bicarbonate Solution
摘 要
采用失重法、电化学阻抗和极化曲线法对不同热处理条件下A3钢在30 g/L的NaHCO3溶液中的耐蚀性能及机理进行了探讨.结果表明:A3钢在该腐蚀介质中腐蚀48 h后,其耐蚀性能的排序为正火态＞淬火态＞退火态＞原始态,这是由于组织结构的变化而引起的.
NaHCO3溶液
热处理
机理
A3 steel
sodium bicarbonate solution
heat treatment
mechanism
Abstract
The effect of heat treatment on corrosion mechanism and corrosion resistance of A3 steel in sodium bicarbonate solution was studied by weight loss testing,EIS and polarization curves.Results show that heat treatment can improve the corrosion resistance of A3 steel.The normalized samples had the best corrosion resistance after 48 hours in sodium bicarbonate solution and the effect was caused by the change of microstructure.
中图分类号 TG172.6 TG174.2
所属栏目 试验研究
基金项目
收稿日期 2008/4/19
修改稿日期 2008/6/18
网络出版日期
作者单位点击查看
引用该论文: LI Xiao-wei,GAO Yan-min. Effect of Heat Treatment on Corrosion Resistance of A3 Steel in Sodium Bicarbonate Solution[J]. Corrosion & Protection, 2009, 30(5): 309～311
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】高延敏,王文,徐永祥,等.有机酸对A3钢腐蚀的影响[J].沈阳:腐蚀科学与防护技术,2002,14(6):326-328.
【2】徐永祥,严川伟,高延敏,等.表面状态和处理对涂层下A3钢腐蚀和涂层失效的影响[J].沈阳:腐蚀科学与防护技术,2003,15(4):208-211.
【3】高延敏,王绍明,徐永祥,等.A3钢在乙酸中的腐蚀行为和机理[J].腐蚀与防护,2006,27(1):11-13.
【2】徐永祥,严川伟,高延敏,等.表面状态和处理对涂层下A3钢腐蚀和涂层失效的影响[J].沈阳:腐蚀科学与防护技术,2003,15(4):208-211.
【3】高延敏,王绍明,徐永祥,等.A3钢在乙酸中的腐蚀行为和机理[J].腐蚀与防护,2006,27(1):11-13.
相关信息