船用锅炉过热管束异常破损分析
Analysis of Abnormal Damage of Ship Boiler Superheat-tubes
摘 要
某型船用主锅炉过热器管束普遍存在短时间非正常破损现象.通过对该主锅炉过热器管束的勘查和腐蚀产物分析,认为破管的主要原因是管壁温度过高、过热蒸气中的氧和氯离子的协同作用结果.据此提出了改进措施和建议.
过热管
锅炉
abnormal corrosion
superheat-tube
boiler
Abstract
The phenomena of abnormal damage of boiler superheat-tubes in some ship are prevalent.The reason of abnormal corrosion was studied by means of survey and analysis of corrosion product.It was concluded that the corrosion damage was due to the high temperatme of tube walls,synergic action of oxygen and chloride in superheated vapor.Some proposals were put forward.
中图分类号 TG172
所属栏目 失效分析
基金项目
收稿日期 2008/4/21
修改稿日期 2008/6/24
网络出版日期
作者单位点击查看
引用该论文: ZHANG Xiao-dong,HU Yu-long,CHEN De-bin,LIU Feng. Analysis of Abnormal Damage of Ship Boiler Superheat-tubes[J]. Corrosion & Protection, 2009, 30(5): 348～351
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李美栓.金属的高温腐蚀[M].北京:冶金工业出版社,2001.
【2】翟金坤.金属高温腐蚀[M].北京:北京航空航天大学出版社,1994.
【3】张承忠.金属的腐蚀与保护[M].北京:冶金工业出版社,1994.
【4】陈君旋.锅炉金属的腐蚀分析与防止[J].腐蚀与防护,2000,21(5):216-217.
【5】舒勇华,王福会,周龙江,等.在500~700 ℃水蒸气和NaCl协同作用下1Cr11Ni2W2MoV钢的腐蚀[J].金属学报,1998,34(5):483-488.
【6】田永淑.工业锅炉常见的腐蚀与防护[J].腐蚀与防护,2000,21(1):32-33.
【2】翟金坤.金属高温腐蚀[M].北京:北京航空航天大学出版社,1994.
【3】张承忠.金属的腐蚀与保护[M].北京:冶金工业出版社,1994.
【4】陈君旋.锅炉金属的腐蚀分析与防止[J].腐蚀与防护,2000,21(5):216-217.
【5】舒勇华,王福会,周龙江,等.在500~700 ℃水蒸气和NaCl协同作用下1Cr11Ni2W2MoV钢的腐蚀[J].金属学报,1998,34(5):483-488.
【6】田永淑.工业锅炉常见的腐蚀与防护[J].腐蚀与防护,2000,21(1):32-33.
相关信息