大型海水循环泵腐蚀与防护技术应用
Application of Corrosion and Protection Technology to Seawater Circle Pumps
摘 要
滨海电厂主循环泵的腐蚀研究及阴极保护技术应用推广在国内已有十余年的历史,因其效果显著,已愈来愈得到生产厂家的重视.目前国内滨海电厂循环水泵的保护主要是:泵内采用涂层加外加电流阴极保护技术:泵外水下部分采用涂层加牺牲阳极保护方法.本文从腐蚀原因分析、外加电流阴极保护技术及应用情况等几方面对海水循环泵的腐蚀与防护进行介绍.
腐蚀
外加电流
防护技术
pump
corrosion
impressed current
protection technology
Abstract
The technology of cathodic protection(CP) has teen applied to circle pumps in power plants at sea coast area for more than ten years in China.At present the main protection technology of circle pumps is coating plus impressed current CP for pump inside,coating and sacrificial anode CP for underwater part of pump outside.In this paper,the corrosion reasons,the impressed current CP technology and its application to circle pumps are discussed.
中图分类号 TG174.41
所属栏目 应用技术
基金项目
收稿日期 2008/6/4
修改稿日期 2008/7/23
网络出版日期
作者单位点击查看
引用该论文: ZHANG Wen-bo,PANG Qi-wei. Application of Corrosion and Protection Technology to Seawater Circle Pumps[J]. Corrosion & Protection, 2009, 30(6): 420～422
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】朱相荣,王相润.金属材料的海洋腐蚀与防护[M].北京:国防工业出版社,1999.
【2】林玉珍,李焕文,雍兴跃,等.海水输送泵的腐蚀与阴极保护技术应用的研究[J].全面腐蚀控制,1996,10(4):8-11.
【3】［美］ F W 芬克,W K 博伊德.海洋环境中金属的腐蚀[M].北京:科学出版社,1976.
【4】于福州.金属材料的耐腐蚀性[M].北京:科学出版社,1982.
【5】GB/T 16166-1996,滨海电厂海水冷却水系统牺牲阳极阴极保护[S].
【6】汪国平,洪栋煌.船舶与钢结构的涂装及防蚀技术[M].北京:国防工业出版社,1993.
【7】庞其伟,曲 政,孟 超.海滨发电厂海水循环泵外加电流保护失效原因及对策[J].热力发电,2004,10(9):72-74.
【2】林玉珍,李焕文,雍兴跃,等.海水输送泵的腐蚀与阴极保护技术应用的研究[J].全面腐蚀控制,1996,10(4):8-11.
【3】［美］ F W 芬克,W K 博伊德.海洋环境中金属的腐蚀[M].北京:科学出版社,1976.
【4】于福州.金属材料的耐腐蚀性[M].北京:科学出版社,1982.
【5】GB/T 16166-1996,滨海电厂海水冷却水系统牺牲阳极阴极保护[S].
【6】汪国平,洪栋煌.船舶与钢结构的涂装及防蚀技术[M].北京:国防工业出版社,1993.
【7】庞其伟,曲 政,孟 超.海滨发电厂海水循环泵外加电流保护失效原因及对策[J].热力发电,2004,10(9):72-74.
相关信息