Effect of a Phosphating Multiple Promoter on Performance of Zinc-series Phosphating Solution at Normal Temperature
摘 要
以磷酸和氧化锌为主要原料,研制了一种常温锌系磷化液.考察了游离酸度、总酸度及自制CT-1复合促进剂对磷化液性能的影响,用红外光谱(IR)对磷化膜的主要成分进行了表征.结果表明,适量的自制CT-1促进剂可以提高磷化膜的耐蚀性,膜的成分以缔合型磷酸盐为主.
Abstract
A normal temperature zinc-series phosphating solution had been developed with phosphor acid and zinc oxide as main raw materials.The effect of free-acidity,total-acidity and multiple promoter on performance of phosphate film was observed by IR.The results showed that suitable self-made CT-1 could increase the anti-corrosion performance of zinc-series phosphate film and the main component of the film was complex phosphate.
中图分类号 TG178 TQ639.1
所属栏目 应用技术
基金项目
收稿日期 2008/7/15
修改稿日期 2008/8/29
网络出版日期
作者单位点击查看
备注陈同云,教授.
引用该论文: CHEN Tong-yun. Effect of a Phosphating Multiple Promoter on Performance of Zinc-series Phosphating Solution at Normal Temperature[J]. Corrosion & Protection, 2009, 30(8): 564~566
被引情况:
【1】余取民,刘琳琪,杨建, "钡盐改性清洁型常温锌锰系磷化液",腐蚀与防护 31, 712-714(2010)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张圣麟,陈华辉,李红玲,等.常温磷化处理技术的研究现状及展望[J].材料保护,2006,39(7):42-44.
【2】蒙文坚.常温锌铁系彩色磷化工艺及应用[J].表面技术,2001,30(1):41-43.
【3】黄霓裳,郭良生.室温加速剂的选择[J].表面技术,1996,25(4):19-21.
【4】黄霓裳,郭良生.新型常温低渣磷化液[J].腐蚀与防护,2001,22(2):61-63.
【5】肖鑫,龙有前.常温高稳定剂彩色磷化工艺研究[J].电镀与精饰,2001,23(2):9-11.
【6】朱立群,付宝智.稀土复合作用常温磷化工艺的研究[J].电镀与涂饰,2001,20(4):8-11.
【2】蒙文坚.常温锌铁系彩色磷化工艺及应用[J].表面技术,2001,30(1):41-43.
【3】黄霓裳,郭良生.室温加速剂的选择[J].表面技术,1996,25(4):19-21.
【4】黄霓裳,郭良生.新型常温低渣磷化液[J].腐蚀与防护,2001,22(2):61-63.
【5】肖鑫,龙有前.常温高稳定剂彩色磷化工艺研究[J].电镀与精饰,2001,23(2):9-11.
【6】朱立群,付宝智.稀土复合作用常温磷化工艺的研究[J].电镀与涂饰,2001,20(4):8-11.
相关信息
标题 | 相关频次 | |
常温钢铁多功能磷化液 | 2 | |
常温铁系磷化工艺研究 | 2 | |
常温下镁锂合金浸锌溶液及一次浸锌 | 2 | |
复合常温磷化促进剂研究 | 2 | |
钢铁的常温磷化液配方优选 | 2 | |
钡盐改性常温锌钙系磷化液 | 1 | |
钡盐改性清洁型常温锌锰系磷化液 | 1 | |
不锈钢氧化皮常温清洗膏 | 1 | |
常温铁系磷化液 | 1 | |
环保型钢铁常温发黑剂的研制 | 1 | |
科学家发明纳米工厂 常温生产半导体纳米晶体 | 1 | |
免水洗常温锰系磷化膜的制备与性能 | 1 | |
一种新型的不锈钢氧化皮常温快速清洗液 | 1 | |
一种新型钢铁表面常温“四合一”除油除锈磷化液 | 1 |