铝导线混合酸阳极氧化绝缘膜工艺
Preparation Technology of Mixed Acid Anodized Insulating layer for Aluminium Wire
摘 要
试验研究了铝扁导线混合酸阳极氧化工艺方法,得到了绝缘性能优良的氧化铝膜.膜层击穿电压达到250V.同传统的硫酸阳极氧化工艺相比,该膜层脆性低、韧性好、槽温范围宽;同草酸阳极氧化工艺相比,该工艺所需时间短、耗能少、生产效率高.可以满足除铁器电磁线圈绕组导线的生产和使用要求.
绝缘
电磁线圈
混合酸
anodization
insulation
electromagnctic coil
mixed acid
Abstract
A mixed acid anodic oxidation process was investigated to prepare insulating layer for aluminium strip conductor.The puncture voltage of insulating layer could reach 250V.Compared with the oxide film made by traditional sulfuric acid anodization,this oxide film had lower brittleness,better ductility and wider bath temperature range.The mixed acid anodization process was energy-saving and high-efficiency than that using oxalic acid anodization process.Producing and using demands of wires without electromagnetic coil winding could be satisfied.
中图分类号 TG174.45
所属栏目 应用技术
基金项目
收稿日期 2008/7/28
修改稿日期 2008/9/1
网络出版日期
作者单位点击查看
引用该论文: WU Jing,JI Jia-ming. Preparation Technology of Mixed Acid Anodized Insulating layer for Aluminium Wire[J]. Corrosion & Protection, 2009, 30(8): 579～581
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】高云震,任继嘉,宁福元.铝合金表面技术[M].北京:冶金出版社,1991:64-68.
【2】曾华梁,吴仲达,陈钧武,等.电镀工艺手册[M].第二版,北京:机械工业出版社,1997:394-395.
【3】刘新田.表面工程[M].第一版,开封:河南大学出版社,2000:232-233.
【4】许旋,罗一帆.添加剂对铝合金阳极氧化膜形成的影响[J].应用化学,2002,19(4):355-358.
【5】田连朋.几种外加离子对铝阳极氧化膜电化学性质的影响[D].北京:北京化工大学博士论文,2006:63.
【2】曾华梁,吴仲达,陈钧武,等.电镀工艺手册[M].第二版,北京:机械工业出版社,1997:394-395.
【3】刘新田.表面工程[M].第一版,开封:河南大学出版社,2000:232-233.
【4】许旋,罗一帆.添加剂对铝合金阳极氧化膜形成的影响[J].应用化学,2002,19(4):355-358.
【5】田连朋.几种外加离子对铝阳极氧化膜电化学性质的影响[D].北京:北京化工大学博士论文,2006:63.
相关信息