温度对铂钽复合阳极电化学性能的影响
Effect of Temperature on Electrochemical Properties of Pt/Ta Composite Anode
摘 要
对铂钽复合阳极在200 mA/cm2的电流密度下进行了恒电流试验,通过测量动电位极化曲线以及电化学阻抗谱,研究了阳极在不同温度海水中的电化学行为,利用扫描电镜(SEM)及能谱仪(EDS)对阳极形貌及成分进行了分析.电化学试验结果表明,铂钽复合阳极能承载较大的电流密度:随温度的降低,法拉第电荷传递电阻增大,阳极电化学催化活性有所下降.SEM分析结果表明,阳极表面有微裂纹,阳极工作时表面有大量气体析出,加速了阳极的溶解.
动电位极化
阻抗
阳极氧化
composite anode
potentiodynamic polarization
impedance
anodic oxidation
Abstract
Pt/Ta composite anode was tested at a constant current density of 200 mA/cm2.The electrochemical properties was characterized by potentindynamic polarization curves and electrochemical impedance spectroscopy (EIS) in seawater at different temperatures,in combination with SEM morphology observation and energy disperse spectroscopy (EDS).The results showed that Pt/Ta composite anode could load large current density.Electrochemical catalytic activity of the anode decreased relatively and the charge transfer resistance of Faradaic process increased evidently at low temperatures.The surface microcrak and the gas evalufron from working anode accelerated the dissolution of anode.
中图分类号 TG174.41
所属栏目 试验研究
基金项目
收稿日期 2008/8/26
修改稿日期 2008/9/24
网络出版日期
作者单位点击查看
引用该论文: LI Qing-yan,YAN Yong-gui,MA Li,ZHAO Cheng. Effect of Temperature on Electrochemical Properties of Pt/Ta Composite Anode[J]. Corrosion & Protection, 2009, 30(9): 652～654
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】贝克曼 W V,施文克 W.阴极保护手册电化学保护的理论与实践[M].北京:化学工业出版社,2005.
【2】郭为民,李文军,陈光章.材料深海环境腐蚀试验[J].装备环境工程,2006,1(3):10-15.
【3】朱相荣,王相润.金属材料的海洋腐蚀与防护[M].北京:国防工业出版社,1999.
【4】王佳,孟洁,唐晓,等.深海环境钢材腐蚀行为评价技术[J].中国腐蚀与防护学报,2007,27(1):1-7.
【5】GB/T 7388-1999,船用辅助阳极技术条件[S].
【6】Lassali T A F,Boodts J F C,Bulhoes L O S.Charging processes and electrocatalytic properties of IrO2/TiO2/SnO2 oxide films investigated by in situ AC impedance measurement[J].Electrochi Acta,1999,44:4203-4216.
【7】黄运涛,彭乔.海水电解用金属氧化物阳极的失活机理[J].稀有金属材料与工程,2006,35(10):1610-1612.
【8】陈长风,路民旭,赵国仙,等.温度、Cl-浓度、Cr元素对N80钢CO2腐蚀电极过程的影响[J].金属学报,2003,39(8):848-854.
【9】曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002:177-190.
【10】黄拔帆,袁宏鸣,骆瑞雪.Cu和Fe在Pt阳极复层中的扩散[J].稀有金属材料与工程,1992,21(3):67-70.
【11】吴荫顺,郑家燊.电化学保护和缓蚀剂应用技术[M].北京:化学工业出版社,2006,162.
【12】Baboian R.Performance of platinum clad columbium impressed current anodes in freshwater[J].Materials Performance,1983,22(12):15-18.
【2】郭为民,李文军,陈光章.材料深海环境腐蚀试验[J].装备环境工程,2006,1(3):10-15.
【3】朱相荣,王相润.金属材料的海洋腐蚀与防护[M].北京:国防工业出版社,1999.
【4】王佳,孟洁,唐晓,等.深海环境钢材腐蚀行为评价技术[J].中国腐蚀与防护学报,2007,27(1):1-7.
【5】GB/T 7388-1999,船用辅助阳极技术条件[S].
【6】Lassali T A F,Boodts J F C,Bulhoes L O S.Charging processes and electrocatalytic properties of IrO2/TiO2/SnO2 oxide films investigated by in situ AC impedance measurement[J].Electrochi Acta,1999,44:4203-4216.
【7】黄运涛,彭乔.海水电解用金属氧化物阳极的失活机理[J].稀有金属材料与工程,2006,35(10):1610-1612.
【8】陈长风,路民旭,赵国仙,等.温度、Cl-浓度、Cr元素对N80钢CO2腐蚀电极过程的影响[J].金属学报,2003,39(8):848-854.
【9】曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002:177-190.
【10】黄拔帆,袁宏鸣,骆瑞雪.Cu和Fe在Pt阳极复层中的扩散[J].稀有金属材料与工程,1992,21(3):67-70.
【11】吴荫顺,郑家燊.电化学保护和缓蚀剂应用技术[M].北京:化学工业出版社,2006,162.
【12】Baboian R.Performance of platinum clad columbium impressed current anodes in freshwater[J].Materials Performance,1983,22(12):15-18.
相关信息