一种新的AZ40镁合金阳极氧化工艺
A New Technology of Anodic Qxidation for Magnesium Alloy AZ40
摘 要
用交流稳压法和正交试验法对AZ40镁合金进行了阳极氧化试验,开发出了一种新型环保型镁合金阳极氧化的电解液配方,添加一种新的成膜添加剂后,成膜速度加快;形成的阳极氧化膜有良好的耐腐蚀性；经过封孔工艺处理后,其自腐蚀电流密度为0.503 μA／cm2；XRD分析表明氧化膜主要由基体元素Mg及其氧化物MgO组成,另外还含有SiO2和镁的硅酸盐；SEM结果显示氧化膜呈完整的陶瓷状态.
阳极氧化
腐蚀
封孔
极化曲线
magnesium alloy
anodic oxidation
corrosion
sealing
polarization curve
Abstract
A new environmentally anodizing electrolyte for AZ40 magnesium alloy was developed by using AC voltage regulator method and orthogonal test.The film had good corrosion resistance and the film forming was rapid by adding a new film-forming additive.After sealing process,the corrosion current density of coating was 0.503 μA/cm2.XRD analysis indicated that the oxide film composed mainly of Mg,MgO,SiO2 and magnesium silicate.SEM analysis showed that the bond between film and substrate of magnesium was good.
中图分类号 TG174.45
所属栏目 应用技术
基金项目
收稿日期 2008/10/15
修改稿日期 2008/12/5
网络出版日期
作者单位点击查看
引用该论文: CHEN Yi-sheng,LIU Yong-dan,ZHU Zhi-yun,LIU Jian-feng,XIONG Shi-xian. A New Technology of Anodic Qxidation for Magnesium Alloy AZ40[J]. Corrosion & Protection, 2009, 30(11): 816～817
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张永君,严川伟,赵桂芹,等.压铸镁合金AZ91D环保型阳极氧化电解液配方研究[J].腐蚀与防护,2002,23(4):148-151.
【2】Oscar K,Danny W.Anodizing of pure magnesium in KOH-Aluminate solutions under sparking[J].J Electrochem Soc,1999,146(5):1757-1761.
【3】周婉秋,单大勇,韩恩厚,等.镁合金无铬化学转化膜的耐蚀性研究[J].材料保护,2002,35(2):12-14.
【4】张永君,严川伟,楼翰一,等.镁及其合金的阳极氧化技术进展[J].腐蚀科学与防护技术,2001,13(4):214-17.
【5】蒋百灵,张淑芬,吴国建.镁合金微弧氧化陶瓷层显微缺陷与相组成及其耐蚀性[J].中国有色金属学报,2002,12(3):454-457.
【2】Oscar K,Danny W.Anodizing of pure magnesium in KOH-Aluminate solutions under sparking[J].J Electrochem Soc,1999,146(5):1757-1761.
【3】周婉秋,单大勇,韩恩厚,等.镁合金无铬化学转化膜的耐蚀性研究[J].材料保护,2002,35(2):12-14.
【4】张永君,严川伟,楼翰一,等.镁及其合金的阳极氧化技术进展[J].腐蚀科学与防护技术,2001,13(4):214-17.
【5】蒋百灵,张淑芬,吴国建.镁合金微弧氧化陶瓷层显微缺陷与相组成及其耐蚀性[J].中国有色金属学报,2002,12(3):454-457.
相关信息