Corrosion Failure Analysis and Protective Measures of Ethylene Unit TS-212 Crude Benzol Reaction Heat Exchanger
摘 要
某乙烯装置TS-212粗苯反应换热器发生腐蚀泄漏,采取X射线衍射、能谱分析、扫描电镜等检测手段,对该管束进行了失效分析,结果表明,TS-212发生的腐蚀主要是由CO2+H2O腐蚀体系所引起的,而系统中存在的O2更加剧了这种腐蚀.另外,腐蚀速率受CO2分压、流速、温度、保护膜和溶液成分等诸多因素的影响,尤其是壳程湍流引发空泡腐蚀产生的冲刷和冲击作用加剧了腐蚀破坏作用.据此结论提出了系统的防治措施.
Abstract
X-ray diffraction (XRD),energy-dispersive spectroscopy (EDS) and scanning electronic microscopy(SEM) were used to analyze the corrosion and leakage reason of the ethylene unit TS-212 crude benzol reaction heat exchanger.The results show that the CO2+H2O corrosion system resulted in the corrosion failure of TS-212 heat exchanger,and O2 existing in this system accelerated the corrosion process.Factors such as partial pressure of CO2,velocity of flow,temperature,protective film,solution composition and so on affected the corrosive rate.A series of protective measures were proposed according to the above results of corrosion analysis.
中图分类号 TG172
所属栏目 腐蚀失效分析
基金项目
收稿日期 2008/12/5
修改稿日期 2009/1/6
网络出版日期
作者单位点击查看
联系人作者邹积强(zoujq@wepec.com)
备注邹积强,高工.
引用该论文: ZHANG Xue-yong,ZOU Ji-qiang. Corrosion Failure Analysis and Protective Measures of Ethylene Unit TS-212 Crude Benzol Reaction Heat Exchanger[J]. Corrosion & Protection, 2009, 30(12): 936~938
被引情况:
【1】李辉辉,胥聪敏,杨东平, "炼油厂重催装置分馏塔顶换热器管束的腐蚀失效分析",机械工程材料 39, 102-106(2015)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】中国石油化工设备管理协会设备防腐专业组.石油化工装置设备腐蚀与防护手册[M].北京:中国石化出版社,1994:3.
【2】王德国,何仁洋,董山英.长距离油、气、水混输管道内壁流动腐蚀的研究进展[J].天然气与石油,2002,20(4):24-29.
【3】龚敏.冲刷腐蚀的某些影响因紊及其研究方法[J].四川轻化工学院学报,1995,8(1):53-59.
【4】张学元,邸超,雷良才.二氧化碳腐蚀与控制[M].北京:化学工业出版社,2000.
【5】付秀勇,胡文革.凝析气田集输管线冲刷腐蚀与防护问题[J].腐蚀与防护,2008,29(8):467-470.
【2】王德国,何仁洋,董山英.长距离油、气、水混输管道内壁流动腐蚀的研究进展[J].天然气与石油,2002,20(4):24-29.
【3】龚敏.冲刷腐蚀的某些影响因紊及其研究方法[J].四川轻化工学院学报,1995,8(1):53-59.
【4】张学元,邸超,雷良才.二氧化碳腐蚀与控制[M].北京:化学工业出版社,2000.
【5】付秀勇,胡文革.凝析气田集输管线冲刷腐蚀与防护问题[J].腐蚀与防护,2008,29(8):467-470.
相关信息