Preparation of Heat and Corrosion Resistant Layer on 304 Austenitic Stainless Steel
摘 要
以SUS304不锈钢为基材,通过电镀沉积镍和高温扩散处理的方法制备耐热防腐蚀层.用扫描电镜、X衍射仪、能谱仪等设备对耐热防腐蚀层进行分析.结果表明:经1050 ℃高温扩散30 min后,不锈钢表面的镀层由机械结合转化为冶金结合,镀层与基材的结合力显著提高.热震试验、盐雾试验和高温氧化试验结果证实,研制的镀层具有高的耐热防腐蚀性能.
Abstract
The heat and corrosion resistant layer was prepared on the surface of SUS304 stainless steel by electric plating Ni and high-temperature diffusion.The properties of the layer were analyzed by scanning electron microscopy(SEM),X-ray diffraction(XRD) and energy spectroscopy.The results showed that the plating on stainless steel transformed from mechanical binding to metallurgical binding and the binding force between coating and substrate was improved greatly after high-temperature diffusion at 1050 ℃ for 30 min.The results of thermal shock test、salt spray test and high-temperature oxidation test showed that the plating had high heat and corrosion resistance.
中图分类号 TG174.44
所属栏目 试验研究
基金项目
收稿日期 2009/1/30
修改稿日期 2009/2/23
网络出版日期
作者单位点击查看
备注邵红红,硕士生导师.
引用该论文: SHAO Hong-hong,SU Bo,ZHANG Liang,ZHANG Jing-wen. Preparation of Heat and Corrosion Resistant Layer on 304 Austenitic Stainless Steel[J]. Corrosion & Protection, 2010, 31(1): 37~39
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘钧泉,宋丽丽.一种不锈钢用涂层研究[J].电镀与涂饰,2006,25(5):35-37.
【2】陈天玉.不锈钢表面处理技术[M].北京:化学工业出版社,2004.
【3】龚利华,崔景海,张禹.热处理对0Cr18Ni9Ti不锈钢耐蚀性的影响[J].腐蚀科学与防护技术,2008,20(1):39-41.
【4】罗宏,龚敏.奥氏体不锈钢的晶间腐蚀[J].腐蚀科学与防护技术,2006,18(5):357-359.
【5】袁涛,贺定勇,蒋建敏.钢结构热喷涂长效防腐蚀技术的研究与发展[J].腐蚀与防护,2008,29(4):207-210.
【6】李冰.奥氏体不锈钢换热管脆性断裂原因浅析[J].全面腐蚀控制,2006,20(3):21-23.
【7】杨伟群,于维平.不锈钢表面高温抗氧化涂层新工艺[J].新技术新工艺,1998,5(38):23-25.
【2】陈天玉.不锈钢表面处理技术[M].北京:化学工业出版社,2004.
【3】龚利华,崔景海,张禹.热处理对0Cr18Ni9Ti不锈钢耐蚀性的影响[J].腐蚀科学与防护技术,2008,20(1):39-41.
【4】罗宏,龚敏.奥氏体不锈钢的晶间腐蚀[J].腐蚀科学与防护技术,2006,18(5):357-359.
【5】袁涛,贺定勇,蒋建敏.钢结构热喷涂长效防腐蚀技术的研究与发展[J].腐蚀与防护,2008,29(4):207-210.
【6】李冰.奥氏体不锈钢换热管脆性断裂原因浅析[J].全面腐蚀控制,2006,20(3):21-23.
【7】杨伟群,于维平.不锈钢表面高温抗氧化涂层新工艺[J].新技术新工艺,1998,5(38):23-25.
相关信息