加热炉空气预热器管破坏原因分析及预防措施

Failure Analyses of Air Preheating Tube of a Heating Furnace and Its Improvement Measures

阎永京

摘要

通过金相检验、X射线衍射分析以及X射线光电子能谱(XPS)分析,得出加热炉空气预热器管破坏原因是硫酸露点腐蚀和高温燃气腐蚀的共同作用所致,并对此提出相应预防措施.

标签失效分析

硫酸露点腐蚀

高温燃气腐蚀

failure analysis

suffuric acid dew point corrosion

high tempreture fired gas corrosion

Abstract

The failure reesons of an air preheating tube were investigatal by using microstructure examination,X-ray diffraction and XPS tests.The results showed that the failure causes of the tube were the co-action of the suffuric acid dew point corrosion and high tempreture fired gas corrosion.Some improvement measures put forward.

中图分类号 TG172.8

所属栏目失效分析

基金项目

收稿日期 2009/7/2

修改稿日期

网络出版日期

作者单位点击查看

引用该论文: YAN Yong-jing. Failure Analyses of Air Preheating Tube of a Heating Furnace and Its Improvement Measures[J]. Corrosion & Protection, 2010, 31(1): 89～91

论文评价

共有人对该论文发表了看法，其中：

人认为该论文很差

人认为该论文较差

人认为该论文一般

人认为该论文较好

人认为该论文很好

分享论文

相关信息

	标题	相关频次
	(NH₄)₂SO₄管线开裂失效的原因	2
	100t汽车车轴断裂分析	2
	12Cr1MoV珠光体耐热钢长期服役中碳化物的变化及对性能的影响	2
	16Co14Ni10Cr2MoE钢制抽筒抓钩开裂失效分析	2
	16Mn集输管线钢在含CO₂凝析气田的腐蚀行为	2
	252 kV GIS机构止动螺栓的断裂失效分析	2
	300 MW机组回转式空气预热器仓格板开裂原因分析	2
	304不锈钢低温分离器开裂原因分析	2
	30CrMnSiA钢螺钉断裂失效分析	2
	30CrMnSiA螺栓失效分析	2
	35CrMo钢带泵轴断裂原因分析	2
	35kV架空输电线路钢芯铝绞线内层铝股线的腐蚀失效分析	2
	3Cr2W8V钢压铸模具断裂分析	2
	3PE防腐蚀层失效分析与寿命预测	2
	40CrNiMo钢剪切闸板刃口断裂的原因	2
	40Cr钢合闸支撑轴弯曲失效分析	2
	40Cr钢汽车半轴断裂失效分析	2
	40Mn18Cr4V钢穿心螺杆断裂分析	2
	4102柴油机喷油泵弹簧断裂原因分析	2
	600 MW超临界电站锅炉末级过热器管爆裂失效分析	2
	60Si2CrA Ⅱ型弹条断裂原因	2
	670t/h锅炉高温过热器管爆裂失效分析	2
	700 mm轧机轧辊断裂失效分析	2
	7075铝合金缸体的失效分析	2
	7075铝合金高锁螺母开裂原因	2
	800H合金旋风分离器壳体失效分析	2
	Cr12MoV钢模具线切割开裂原因分析	2
	Cr12不锈钢零件表面裂纹分析	2
	Cr12钢水胀模具底座断裂原因分析	2
	DN50不锈钢波纹软管开裂失效分析	2