柴油加氢精制装置分离器管道开裂分析
Failure Analysis for the Rupture of Segregator Pipeline in Diesel Hydrofining Unit
摘 要
采用宏观检查、金相显微分析、直读光谱分析、扫描电镜(SEM)和电子能谱分析(EDS)等方法,对柴油加氢精制装置分离器管道开裂的原因进行分析.结果表明,硫化氢应力腐蚀开裂(SSCC)是造成管道开裂的根本原因,建议对管道的材料与热处理工艺进行重新选择.
硫化氢应力腐蚀
热处理
金相分析
pipeline steel
SSCC
heat treatment
metallographic analysis
Abstract
The methods of visual inspection,metallographic analysis,direct reading spectrometric analysis,SEM and EDS were adopted to study the rupture of a segregator pipeline in diesel hydrofining unit.Results indicated that sulfide stress corrosion cracking (SSCC) was the main reason for the cracking of pipeline steel.It is suggesed to reselect the material or heat treatment for the pipeline.
中图分类号 TG172.9
所属栏目 失效分析
基金项目
收稿日期 2009/2/24
修改稿日期 2009/4/3
网络出版日期
作者单位点击查看
备注丁毅,硕士研究生.
引用该论文: CHEN Xu,WANG Yu-shun,DING Yi,MA Li-qun. Failure Analysis for the Rupture of Segregator Pipeline in Diesel Hydrofining Unit[J]. Corrosion & Protection, 2010, 31(2): 176～178
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Smith L M,Crolet J L,Eliassen S,et al.Techniacal forum: Review of sour service definitions,Part 1[J].Materials Performance & Design,1997,36(4),66-67.
【2】卢志明.典型压力容器用钢在湿硫化氢环境中的应力腐蚀开裂研究[D].杭州:浙江大学化工机械研究所,2003.
【3】上海市机械制造工艺研究所.金相分析技术[M].上海:上海科学技术文献出版社,1987.
【4】胡光立,谢希文.钢的热处理[M].西安:西北工业大学出版社,2004.
【5】左演生,陈文哲,梁伟.材料现代分析方法[M].北京:北京工业大学出版社,2000.
【2】卢志明.典型压力容器用钢在湿硫化氢环境中的应力腐蚀开裂研究[D].杭州:浙江大学化工机械研究所,2003.
【3】上海市机械制造工艺研究所.金相分析技术[M].上海:上海科学技术文献出版社,1987.
【4】胡光立,谢希文.钢的热处理[M].西安:西北工业大学出版社,2004.
【5】左演生,陈文哲,梁伟.材料现代分析方法[M].北京:北京工业大学出版社,2000.
相关信息