高酸性气田缓蚀剂加注方式的模拟试验
Simulation Experiment of Different Injection Modes of High Sour Gas Well Corrosion Inhibitor
摘 要
在模拟高酸性气田集输系统条件下,研究了不同加注方式下咪唑啉和有机胺复配缓蚀剂的缓蚀效果,用扫描电镜和X射线衍射仪对试验结果进行了分析,结果表明,三种加注方式下缓蚀率均在75%以上,涂膜+批加注条件下缓蚀效果最好.
缓蚀剂
加注方式
high sour gas well
corrosion inhibitor
injection mode
Abstract
The effect of injection modes on corrosion inhinition efficiency of the imidazoline and organic amine comlpex inhibitor under the condition of simulating gas-gathering line system of high sour gas well was evaluated by using SEM and XRD.The results indicated that the corrosion inhibition efficiency for three different injection modes was all above 75% and the mode of coating + one-off injection was the best.
中图分类号 TG174.42 TE983
所属栏目 应用技术
基金项目
收稿日期 2009/5/26
修改稿日期 2009/6/30
网络出版日期
作者单位点击查看
备注陈洪杰,工程师.
引用该论文: CHEN Hong-jie,WANG Shen-yang,LIU Ai-shuang,LIU Hao,DU Yan-min. Simulation Experiment of Different Injection Modes of High Sour Gas Well Corrosion Inhibitor[J]. Corrosion & Protection, 2010, 31(4): 321～323
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】于建辉,彭乔.MZL-1型酸洗缓蚀剂配方及性能研究[J].腐蚀与防护,2004,25(1):465-467.
【2】刘建平,李正奉,周晓湘.一种咪唑啉缓蚀剂在碳钢表面成膜的电化学研究[J].腐蚀科学与防护技术,2003,15(5):17-19.
【3】余伟明,王湘,刘群.低温水系统绿色环保型缓蚀剂的研究[J].腐蚀与防护,2003,24(6):13-15.
【4】谷宁,李春梅.表面活性剂对碳钢的缓蚀作用及与缓蚀剂的协同效应[J].表面技术,2003,32(1):60-61.
【5】郭良生,石小燕,黄霓裳,等.海水中磷酸三乙醇胺-磷酸二氢盐对钢铁的缓蚀作用[J].材料保护,1997,30(8):13-14.
【6】王成达,严密林,赵新伟,等.油气田开发中H2S/CO2腐蚀研究进展[J].西安石油大学学报,2005,20(5):66-70.
【2】刘建平,李正奉,周晓湘.一种咪唑啉缓蚀剂在碳钢表面成膜的电化学研究[J].腐蚀科学与防护技术,2003,15(5):17-19.
【3】余伟明,王湘,刘群.低温水系统绿色环保型缓蚀剂的研究[J].腐蚀与防护,2003,24(6):13-15.
【4】谷宁,李春梅.表面活性剂对碳钢的缓蚀作用及与缓蚀剂的协同效应[J].表面技术,2003,32(1):60-61.
【5】郭良生,石小燕,黄霓裳,等.海水中磷酸三乙醇胺-磷酸二氢盐对钢铁的缓蚀作用[J].材料保护,1997,30(8):13-14.
【6】王成达,严密林,赵新伟,等.油气田开发中H2S/CO2腐蚀研究进展[J].西安石油大学学报,2005,20(5):66-70.
相关信息