Mn2+对镀锌板磷化的影响
Effect of Mn2+ on Phosphating of Galvanized Steel
摘 要
通过开路电位-时间曲线和扫描电镜(SEM)的方法研究了镀锌板在含有不同浓度Mn2+磷化液中的磷化成膜过程.结果表明,在磷化液中添加Mn2+,磷化初始电位降低,有利于磷化膜的形成;当Mn(NO3)2含量为0.6g/L时,所生成的磷化膜结晶细化,均匀致密.
镀锌板
Mn2+
结晶
phosphating
galvanized steel
Mn2+
crystal
Abstract
The phosphating process of galvanized steel in phosphating solution with different contents of Mn2+ was investigated by means of open circuit potential-time curves and scanning electron microscopy (SEM).The results showed that Mn2+ in phosphating solution could decrease the initial potential of phosphating and promote the formation of phosphating coating.When the content of Mn(NO3)2 in phosphating solution was 0.6 g/L,the crystals of the phosphate were fine and the phosphating coating formed was uniform and compact.
中图分类号 TG178
所属栏目 应用技术
基金项目 河南省自然科学研究项目(2008A150016);新乡市科技发展计划(07G058)
收稿日期 2009/7/6
修改稿日期 2009/8/31
网络出版日期
作者单位点击查看
引用该论文: ZHANG Sheng-lin,ZHANG Xiao-lin,MA Qiang,LI Wei-wei. Effect of Mn2+ on Phosphating of Galvanized Steel[J]. Corrosion & Protection, 2010, 31(6): 466～468
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李新立.金属磷化技术回顾与展望[J].材料保护,2001,33(1):71-73.
【2】陈慕祖.涂装技术镀锌钢板涂装中的缺陷与改进[J].涂料工业,2003,33(1):30-34.
【3】Ogle K,Tomand A.The Alkaline Stability of Phosphate Coatings I: Atomic Emission Spectroelectrochemistry[J].Corrosion Science,2004,46(4):979-995.
【4】胡美芳.低锌磷化工艺研究[J].腐蚀与防护,1993,14(6):284-289.
【5】吴文镶.锌系磷化液成膜条件及技术改进[J].腐蚀与防护,2007,28(3):132-134,137.
【6】Donofrio J.Zinc phosphating[J].Metal Finishing,2000,98(6):60-73.
【7】陈颖敏,田雷,武洋,等.锈蚀输电杆塔涂装前处理磷化液配方[J].腐蚀与防护,2006,27(6):294-296.
【8】徐惠芳.低温磷化膜形成过程的研究[J].材料保护,1995,28(6):17-19.
【2】陈慕祖.涂装技术镀锌钢板涂装中的缺陷与改进[J].涂料工业,2003,33(1):30-34.
【3】Ogle K,Tomand A.The Alkaline Stability of Phosphate Coatings I: Atomic Emission Spectroelectrochemistry[J].Corrosion Science,2004,46(4):979-995.
【4】胡美芳.低锌磷化工艺研究[J].腐蚀与防护,1993,14(6):284-289.
【5】吴文镶.锌系磷化液成膜条件及技术改进[J].腐蚀与防护,2007,28(3):132-134,137.
【6】Donofrio J.Zinc phosphating[J].Metal Finishing,2000,98(6):60-73.
【7】陈颖敏,田雷,武洋,等.锈蚀输电杆塔涂装前处理磷化液配方[J].腐蚀与防护,2006,27(6):294-296.
【8】徐惠芳.低温磷化膜形成过程的研究[J].材料保护,1995,28(6):17-19.
相关信息