Failure Analysis of Steam Distributor in Waste Caustic Treatment Reactor

马小明

胡林星

摘要

通过材料化学成分分析、扫描电镜、能谱分析、金相检验等手段,对废碱处理塔蒸汽分布器失效原因进行了检验和分析,认为蒸汽分布器失效是由高温硫腐蚀及流体冲刷联合作用所致.为防止事故的重复发生,建议选择耐硫腐蚀的高铬含铝稀土合金或使用专用涂层、改进分布器结构设计等.

标签废碱

蒸汽分布器

纯镍

高温硫腐蚀

冲蚀

waste caustic

steam distributor

pure Ni

high-temperature sulfur corrosion

erosion

Abstract

The failure of steam distributor in waste caustic reactor was investigated by analyses of chemical composition,SEM,EDS and metallography.It was concluded that high-temperature sulfur corrosion and fluid erosion were the main causes of the failure,and corresponding improvement measures were put forward.

中图分类号 TG172.8

所属栏目失效分析

基金项目

收稿日期 2009/7/23

修改稿日期 2009/8/20

网络出版日期

作者单位点击查看

联系人作者马小明(mmxmma@scut.edu.cn)

引用该论文: MA Xiao-ming,HU Lin-xing. Failure Analysis of Steam Distributor in Waste Caustic Treatment Reactor[J]. Corrosion & Protection, 2010, 31(6): 494～496

论文评价

共有人对该论文发表了看法，其中：

人认为该论文很差

人认为该论文较差

人认为该论文一般

人认为该论文较好

人认为该论文很好

分享论文

参考文献

【1】中国石油化工设备管理协会.石油化工装置设备腐蚀与防护手册[M].北京:中国石化出版社,1994:67-72.

【2】李美栓.金属的高温腐蚀[M].北京:北京冶金工业出版社,2001:21.

相关信息

	标题	相关频次
	高速离心式压缩机叶片断裂失效分析	4
	API油管接箍液固两相流体冲蚀数值模拟	2
	HVAF喷涂WC-10Co4Cr涂层及其性能	2
	N80油套管钢在质量分数3.5% NaCl溶液中的冲蚀行为	2
	材料冲蚀磨损的数值模拟研究现状及展望	2
	大功率风力发电机增速齿轮断裂原因分析	2
	氮气钻井过程中的耐冲蚀涂层	2
	氮气钻井过程中井口多功能四通的使用寿命	2
	典型酸性天然气对16Mn钢的冲刷腐蚀影响	2
	段塞流下携砂水平弯管的冲蚀试验	2
	高速双螺杆挤出机螺杆轴断裂失效分析	2
	高温高硫油气管线的腐蚀分析及对策	2
	核电厂二回路冷却系统的冲蚀管理	2
	华南酸性土壤中管线钢腐蚀的在线监测与分析	2
	基于CFD软件的管道弯头冲蚀数值模拟及弯头测厚布点优化	2
	基于斯托克斯数的弯管冲蚀数值模拟	2
	甲酸钠尾气吸收塔失效分析	2
	减压分馏塔塔顶蒸汽喷射泵的失效原因	2
	聚氨酯增韧改性环氧树脂粘接SiC颗粒耐磨涂层的耐冲蚀性能	2
	聚丙烯挤出机螺杆轴断裂失效分析	2
	炼油厂减粘装置加热炉辐射段炉管失效分析	2
	笼套式控制节流阀失效机理研究	2
	某气田地面集输管线的腐蚀原因及控制措施	2
	某油田地面集输管道弯头腐蚀的原因	2
	镍基合金6690换热管应力腐蚀开裂	2
	气化炉煤粉烧嘴Inconel 600开裂原因	2
	汽轮机叶片断裂原因分析	2
	氢气压缩机活塞杆断裂失效分析	2
	胜利海上油田输送管的冲蚀特性	2
	石脑油管线承插焊接管断裂失效的原因	2