Hydrogen Damage Properties of Low Alloy Steel 16Mn in H2S Environment
摘 要
根据NACE TM0284标准对16Mn低合金钢在含饱和H2S的标准A溶液中的氢损伤性能进行了研究.利用CHI660C电化学测试系统对16Mn钢腐蚀渗氢前后的电化学性能进行测量.结果表明,16Mn钢渗氢量较高,对氢致开裂(HIC)较敏感,试样出现了典型的阶梯状HIC裂纹.腐蚀渗氢后试样的自腐蚀电位明显负移,自腐蚀电流密度增大,使得阳极溶解速率增加,材料耐蚀性能降低.16Mn钢P、Mn、S的高含量决定了其特殊的组织性能——高浓度缺陷,致使其氢损伤较严重.
Abstract
According to NACE TM0284,the hydrogen damage properties of low alloy steel 16Mn were investigated in solution A saturated with H2S.The electrochemical properties of 16Mn steel were measured.The results showed that the amount of hydrogen(H) permeation was high and 16Mn steel was sensitive to HIC,which leaded to the typicall ladder-shaped HIC cracks in 16Mn steel.The corrosion potential was shifted negatively and the corrosion current density was higher after H permeation than that without H permeation.The major reason for the formation of defects was the high contents of P,Mn and S in 16Mn steel.
中图分类号 TG172.8
所属栏目 试验研究
基金项目 国家自然科学基金项目(50601029,50771104)资助
收稿日期 2009/8/3
修改稿日期 2010/1/23
网络出版日期
作者单位点击查看
备注蔡晓文,硕士研究生.
引用该论文: CAI Xiao-wen,GE Lei,CHEN Chang-feng. Hydrogen Damage Properties of Low Alloy Steel 16Mn in H2S Environment[J]. Corrosion & Protection, 2010, 31(7): 520~522
被引情况:
【1】殷振兴, "东-黄管线在役16Mn钢的力学性能及腐蚀行为",腐蚀与防护 33, 251-254(2012)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈奇志,褚武扬,乔利杰,等.氢致微裂纹形核的透射电镜原位观察透电原位观察[J].科学通报,1994,39(10):899-902.
【2】蒋兴钢,褚武扬,肖纪美.氢促进孔洞的形核机理[J].中国科学A辑,1994,26(6):668-673.
【3】周琦,季根顺,杨瑞成,等.管线钢中带状组织与氢致开裂[J].甘肃工业大学学报,2002,28(2):30-33.
【4】李明,李晓刚,陈钢,等.16Mn(HIC)钢硫化物应力腐蚀开裂实验研究[J].北京科技大学学报,2007,29(3):282-287.
【5】Pumphrey P H.The role of sulfide inclusions in hydrogen entry during the exposure of steels to acids[J].Corrosion,1980,36(10):537-543.
【6】Taira,Parkins R N.Factors influcencing strees corrosion cracking grouth kinetics[J].Corrosion,1987,43(3):130-139.
【7】褚武扬,乔利杰,陈奇志,等.断裂与环境断裂[M].北京:科学出版社,2000:117-120.
【8】戴鸿平,吴辉煌,周绍民.金属中缺陷对电化学渗氢的影响[J].厦门大学学报自然科学版,1987,26(5):575-578.
【2】蒋兴钢,褚武扬,肖纪美.氢促进孔洞的形核机理[J].中国科学A辑,1994,26(6):668-673.
【3】周琦,季根顺,杨瑞成,等.管线钢中带状组织与氢致开裂[J].甘肃工业大学学报,2002,28(2):30-33.
【4】李明,李晓刚,陈钢,等.16Mn(HIC)钢硫化物应力腐蚀开裂实验研究[J].北京科技大学学报,2007,29(3):282-287.
【5】Pumphrey P H.The role of sulfide inclusions in hydrogen entry during the exposure of steels to acids[J].Corrosion,1980,36(10):537-543.
【6】Taira,Parkins R N.Factors influcencing strees corrosion cracking grouth kinetics[J].Corrosion,1987,43(3):130-139.
【7】褚武扬,乔利杰,陈奇志,等.断裂与环境断裂[M].北京:科学出版社,2000:117-120.
【8】戴鸿平,吴辉煌,周绍民.金属中缺陷对电化学渗氢的影响[J].厦门大学学报自然科学版,1987,26(5):575-578.
相关信息