三种环氧改性聚氨酯基低红外发射率涂层的腐蚀电化学行为
Electrochemical Corrosion Behavior of Three PU-based Low Infrared Emissivity Coatings Modified by EP
摘 要
采用电化学阻抗谱(EIS)研究了以环氧树脂(EP)、改性聚氨酯(PU)为粘合剂,铜粉、硅烷偶联剂改性铜粉、丙烯酸改性铜粉为填料的三种低红外发射率涂料在模拟海水环境(3.5% NaCl溶液)中的电化学腐蚀行为,并比较了这三种涂层体系的防腐蚀性能.结果表明,浸泡初期,铜粉填充环氧改性聚氨酯基涂料表现出较好的防腐蚀性能,但随着浸泡时间延长其失效速度加快,在整个浸泡过程中防腐蚀性能最差.根据涂层电阻(Rcoat)和涂层特征频率(fb)推测,丙烯酸改性铜粉填充环氧改性聚氨酯基涂料的防腐蚀性能优于硅烷偶联剂改性铜粉填充环氧改性聚氨酯基涂料.
电化学阻抗谱
腐蚀
low infrared emissivity coating
EIS
corrosion
Abstract
Electrochemical impedance spectroscopy(EIS) technique was used to investigate the electrochemical corrosion behavior of three low infrared emissivity coatings with polyurethane(PU) modified by epoxy(EP) as adhesive agent,Cu powders,Cu powders modified by silane couple agent,and Cu powders modified by acrylic acid as fillers in simulated sea water(3.5% NaCl).And the corrosion resistance of the three coating systems was compared.The results showed that at the initial stage of immersion,the coating with Cu powders as filler showed relatively good corrosion resistance,but its failure rate was speeded up as immersion time inceeased,throughout the immersion process it showed the worst corrosion resistance.According to coating resistance (Rcoat) and characteristic frequency of coating (fb),the corrosion resistance of the coating filled by acrylic acid modified Cu powders was the best.
中图分类号 V250.3 TB34
所属栏目 试验研究
基金项目
收稿日期 2009/8/19
修改稿日期 2009/9/7
网络出版日期
作者单位点击查看
备注李澄,教授.
引用该论文: ZHANG Chi,LI Cheng,XU Guo-yue,CHEN Sai-shan. Electrochemical Corrosion Behavior of Three PU-based Low Infrared Emissivity Coatings Modified by EP[J]. Corrosion & Protection, 2010, 31(7): 532～535
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】邓朝霞,叶代勇,魏丹,等.环氧改性水性聚氨酯的合成工艺及性能[J].涂料工业,2007,37(4):37-40.
【2】王春艳,朱传方,万婷,等.环氧改性脂肪族水性聚氨酯的合成与性能[J].应用化学,2006,23(4):441-443.
【3】余慧娟,徐国跃,沈轩,等.8-14 μm波段低发射率涂料的制备与优化研究[J].兵器材料科学与工程,2008,31(6):49-52.
【4】张凯,马艳,范敬辉,等.低发射率红外隐身涂料研究进展[J].化学推进剂与高分子材料,2008,6(1):21-25.
【5】张鉴清,孙庆国,曹楚南.评价有机涂层防护性能的EIS数据处理[J].腐蚀科学与防护技术,1994,6(4):318-325.
【6】何杰,阎瑞,马世宁.电化学方法研究环氧涂层/基体在3.5% NaCl溶液中的腐蚀行为[J].中国表面工程,2006,19(2):47-50.
【7】Oliveira C G,Ferreira M G S.Ranking high-quality paint systems using EIS(Ⅰ)[J].Intact coatings Corros.Sci,2003,45:139-147.
【8】周瑶,孙丽娜,万平玉,等.铝镁阳极屏蔽型涂料涂层的交流阻抗图谱[J].腐蚀与防护,2008,39(3):128-132.
【9】张玉玺.EIS法评价有机涂层耐蚀性能的应用研究进展[J].当代化工,2007,36(5):516-534.
【10】张鉴清,张昭,王建明,等.交流阻抗分析系统[J].中国腐蚀与防护学报,2001,21(5):310-313.
【11】刘斌,李瑛,王福会.添加纳米锌粉环氧涂层腐蚀电化学行为[J].腐蚀科学与防护技术,2004,16(1):9-12.
【12】Liu K T,Duh L G.Electrochemical impedance study of TiAlN film coating on a Ni-based alloy in 0.9% NaCl[J].J Mater sci,2008,43:3589-3595.
【13】刘旭文,熊金平,曹京宜,等.EIS法研究3种配套涂层体系的腐蚀电化学行为[J].化工学报,2008,59(3):66.
【14】曹京宜,熊金平,李水冰,等.利用EIS高频区参数评价两种环氧涂层的性能[J].化工学报,2008,59(11):2851-2856.
【15】吴丽蓉,胡学文,许崇武.用EIS 快速评估有机涂层防护性能的方法[J].腐蚀科学与防护技术,2000,12(3):380-481.
【2】王春艳,朱传方,万婷,等.环氧改性脂肪族水性聚氨酯的合成与性能[J].应用化学,2006,23(4):441-443.
【3】余慧娟,徐国跃,沈轩,等.8-14 μm波段低发射率涂料的制备与优化研究[J].兵器材料科学与工程,2008,31(6):49-52.
【4】张凯,马艳,范敬辉,等.低发射率红外隐身涂料研究进展[J].化学推进剂与高分子材料,2008,6(1):21-25.
【5】张鉴清,孙庆国,曹楚南.评价有机涂层防护性能的EIS数据处理[J].腐蚀科学与防护技术,1994,6(4):318-325.
【6】何杰,阎瑞,马世宁.电化学方法研究环氧涂层/基体在3.5% NaCl溶液中的腐蚀行为[J].中国表面工程,2006,19(2):47-50.
【7】Oliveira C G,Ferreira M G S.Ranking high-quality paint systems using EIS(Ⅰ)[J].Intact coatings Corros.Sci,2003,45:139-147.
【8】周瑶,孙丽娜,万平玉,等.铝镁阳极屏蔽型涂料涂层的交流阻抗图谱[J].腐蚀与防护,2008,39(3):128-132.
【9】张玉玺.EIS法评价有机涂层耐蚀性能的应用研究进展[J].当代化工,2007,36(5):516-534.
【10】张鉴清,张昭,王建明,等.交流阻抗分析系统[J].中国腐蚀与防护学报,2001,21(5):310-313.
【11】刘斌,李瑛,王福会.添加纳米锌粉环氧涂层腐蚀电化学行为[J].腐蚀科学与防护技术,2004,16(1):9-12.
【12】Liu K T,Duh L G.Electrochemical impedance study of TiAlN film coating on a Ni-based alloy in 0.9% NaCl[J].J Mater sci,2008,43:3589-3595.
【13】刘旭文,熊金平,曹京宜,等.EIS法研究3种配套涂层体系的腐蚀电化学行为[J].化工学报,2008,59(3):66.
【14】曹京宜,熊金平,李水冰,等.利用EIS高频区参数评价两种环氧涂层的性能[J].化工学报,2008,59(11):2851-2856.
【15】吴丽蓉,胡学文,许崇武.用EIS 快速评估有机涂层防护性能的方法[J].腐蚀科学与防护技术,2000,12(3):380-481.
相关信息