Self-catalytic Action in Pitting Propagation Process of Low Alloy Steels
摘 要
选用了4种低合金钢,通过模拟闭塞腐蚀电池试验,考察了闭塞区溶液条件的变化对闭塞阳极腐蚀溶解速度的影响.结果表明,随着孔内FeCl2浓度增加,pH值下降,阳极腐蚀溶解的速率下降.自催化酸化作用仅是说明在闭塞电池中,溶液酸化保持了金属表面的活化状态,使孔内金属可继续溶解和水解,从而使腐蚀溶解主要集中在孔内而导致蚀孔不断扩展.其所需要的条件是孔外阴极区电位要明显高于孔内电位.
Abstract
Four kinds of low alloy steels had been selected and the effects of solution conditions in the occluded area on corrosion of occluded anode had been studied by means of occluded corrosion cell (OCC) testing.The results indicated that with the increase of FeCl2 concentration and decrease of pH the corrosion rate of anodic metal decreased.Self-catalytic acidification action could be explained as follows: the surface activation of the metal was maintained by the solution acidification,which made the metal dissolve and hydrolyze continuously.Consequently,the corrosion was concentrated in the pit and the pit propagated.The necessary condition was that the potential of cathode out of the pit was more positive than that of anode in side of the pit.
中图分类号 TG171
所属栏目 试验研究
基金项目
收稿日期 2009/8/27
修改稿日期 2009/11/12
网络出版日期
作者单位点击查看
备注杨铁军,工程师.
引用该论文: YANG Tie-jun,LI Guo-ming,CHEN Shan,CHANG Wan-shun,CHEN Xue-qun. Self-catalytic Action in Pitting Propagation Process of Low Alloy Steels[J]. Corrosion & Protection, 2010, 31(7): 540~541
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】魏宝明编.金属腐蚀理论及应用[M].北京:化学工业出版社,1984.
【2】陈鸿海编.金属腐蚀学[M].北京:北京理工大学出版社,1995.
【3】杨武等编著.金属的局部腐蚀[M].北京:化学工业出版社,1995.
【4】陈学群,常万顺,孔小东等.硫化物夹杂对低碳钢点蚀扩展的影响[J].中国腐蚀与防护学报,2000,20(2):65-73.
【5】李国明,陈学群,常万顺,等.闭塞电池方法研究[C]//全国腐蚀电化学进展与应用学术研讨会论文集,昆明,2000.
【6】Sathler L,Muylder J V,Pourbaix M.Electrochemical behavior of iron in localized corrosion cells in the presence of chloride[C]//The Proceeding of the Seventh International Congress of Metallic Corrosion.Toronto:1978:705-718.
【2】陈鸿海编.金属腐蚀学[M].北京:北京理工大学出版社,1995.
【3】杨武等编著.金属的局部腐蚀[M].北京:化学工业出版社,1995.
【4】陈学群,常万顺,孔小东等.硫化物夹杂对低碳钢点蚀扩展的影响[J].中国腐蚀与防护学报,2000,20(2):65-73.
【5】李国明,陈学群,常万顺,等.闭塞电池方法研究[C]//全国腐蚀电化学进展与应用学术研讨会论文集,昆明,2000.
【6】Sathler L,Muylder J V,Pourbaix M.Electrochemical behavior of iron in localized corrosion cells in the presence of chloride[C]//The Proceeding of the Seventh International Congress of Metallic Corrosion.Toronto:1978:705-718.
相关信息