Corrosion Resistance of Carbon Nanotube/Pb-Sn Alloy Composite Coating
摘 要
用复合电沉积方法在黄铜片上制备了碳纳米管/铅锡合金新型减摩复合镀层,对铅锡镀层和碳纳米管/铅锡复合镀层在3.0%(质量分数,下同) HCl、10% NaOH和3.5% NaCl溶液中的极化曲线和电化学阻抗进行了研究.结果表明,碳纳米管/铅锡复合镀层在以上三种介质中的腐蚀电位均有提高,其中,在3.5% NaCl溶液中提高明显,从-0.592 V(SCE)上升到-0.535 V(SCE);复合镀层有更高的电化学阻抗.碳纳米管的添加能提高铅锡镀层的耐蚀性能.
Abstract
A carbon nanotube/Pb-Sn alloy new anti-friction composite coating was prepared on a brass sheet by electro-deposition technology.The polarization curves and electrochemical impedance spectroscopy of the Pb-Sn coating and carbon nanotube/Pb-Sn composite coating were tested in 3.0% HCl,10% NaOH and 3.5% NaCl solutions.The results showed that the corrosion potential of the carbon nanotube/Pb-Sn composite coating increased in the three kinds of corrosion media,especially in 3.5% NaCl solution,it increased from -0.592 V(SCE) to -0.535 V(SCE).In addition,the composite coating had higher electrochemical impedance.Carbon nanotubes can improve the corrosion resistance of Pb-Sn plating coatings.
中图分类号 TG174.44
所属栏目 试验研究
基金项目 国家自然科学基金项目(50775041);广东省自然科学基金项目(05001804);广东省科技计划项目(2008B010400029)
收稿日期 2009/12/7
修改稿日期 2009/12/20
网络出版日期
作者单位点击查看
备注胡正西,讲师.
引用该论文: HU Zheng-xi,JIE Xiao-hua,LU Guo-hui. Corrosion Resistance of Carbon Nanotube/Pb-Sn Alloy Composite Coating[J]. Corrosion & Protection, 2010, 31(10): 745~748
被引情况:
【1】于佃荣,江强,周细应, "溅射气压对Al-Sn-Cu涂层电化学性能的影响",腐蚀与防护 33, 952-954(2012)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张宝义,黄爱华.内燃机轴瓦损坏的形式特征、原因与预防(1)[J].汽车技术,2004(3):28-32.
【2】赵海军,刘磊,朱建华,等.复合电铸制备Ni-石墨复合材料工艺及其沉积机理[J].复合材料学报,2005,22(3):92-97.
【3】黄仲佳,熊党生.Ni-PS-MoS2复合镀层的制备及摩擦磨损性能[J].郑州大学学报,2008,9(24):42-46.
【4】Li X,Li Z.Nano-sized Si3N4 reinforced NiFe nanocomposites by electroplating[J].Mater Sci Eng,2003,A 358:107-109.
【5】何方波,陈斌,梁琨,等.正交试验优化Ni-W-PTFE复合电镀工艺[J].电镀与涂饰,2008,27(9):4-6.
【6】Bhushan B,Israelachvili J,Landman U.Nanotribology: friction,wear,and lubrication at the atomic scale[J].Nature,1995(374):607-616.
【7】Sheehan P E,Lieber C M.Nanotribology and nanofabrication of MoO3 structures by atomic force microscopy[J].Science,1996(272):1158-1161.
【8】Schwarz U D,Zworner O,Koster P,et al.Quantiative analysis of the frictional properties of solid materials at low loads.I.carbon compounds[J].Phys Rev B 1997(56):6987-6996.
【9】Chen X H,Chen C S,Xiao H N,et al.Dry friction and wear characteristics of nickel/carbon nanotube electroless composite deposits[J].Tribol.Int,2006(39):22-28.
【10】Chen X H,Chen C S,Xiao H N,et al.Corrosion behavior carbon nanotubes-Ni composite coating[J].Surface and Coatings Technology,2005(191):351-356.
【11】Yang Z,Xu H,Shi Y L,et al.The fabrication and corrosion behavior of electroless Ni-P-carbon nanotubes composite coatings[J].Materials Research Bulletin,2005(40):1001-1009.
【12】An B G,Li L X,Li H X.Electrodeposition in the Ni-plating bath containing multi-walled carbon nanotubes[J].Materials Chemistry and Physics,2008(110):481-485.
【13】徐关青,张承端.轴瓦电镀层孔洞原因分析及对策[J].汽车工艺与材料,2000(08):40-42.
【2】赵海军,刘磊,朱建华,等.复合电铸制备Ni-石墨复合材料工艺及其沉积机理[J].复合材料学报,2005,22(3):92-97.
【3】黄仲佳,熊党生.Ni-PS-MoS2复合镀层的制备及摩擦磨损性能[J].郑州大学学报,2008,9(24):42-46.
【4】Li X,Li Z.Nano-sized Si3N4 reinforced NiFe nanocomposites by electroplating[J].Mater Sci Eng,2003,A 358:107-109.
【5】何方波,陈斌,梁琨,等.正交试验优化Ni-W-PTFE复合电镀工艺[J].电镀与涂饰,2008,27(9):4-6.
【6】Bhushan B,Israelachvili J,Landman U.Nanotribology: friction,wear,and lubrication at the atomic scale[J].Nature,1995(374):607-616.
【7】Sheehan P E,Lieber C M.Nanotribology and nanofabrication of MoO3 structures by atomic force microscopy[J].Science,1996(272):1158-1161.
【8】Schwarz U D,Zworner O,Koster P,et al.Quantiative analysis of the frictional properties of solid materials at low loads.I.carbon compounds[J].Phys Rev B 1997(56):6987-6996.
【9】Chen X H,Chen C S,Xiao H N,et al.Dry friction and wear characteristics of nickel/carbon nanotube electroless composite deposits[J].Tribol.Int,2006(39):22-28.
【10】Chen X H,Chen C S,Xiao H N,et al.Corrosion behavior carbon nanotubes-Ni composite coating[J].Surface and Coatings Technology,2005(191):351-356.
【11】Yang Z,Xu H,Shi Y L,et al.The fabrication and corrosion behavior of electroless Ni-P-carbon nanotubes composite coatings[J].Materials Research Bulletin,2005(40):1001-1009.
【12】An B G,Li L X,Li H X.Electrodeposition in the Ni-plating bath containing multi-walled carbon nanotubes[J].Materials Chemistry and Physics,2008(110):481-485.
【13】徐关青,张承端.轴瓦电镀层孔洞原因分析及对策[J].汽车工艺与材料,2000(08):40-42.
相关信息