摘 要
为选择某型特种装备的表面防腐蚀涂层,利用电化学阻抗谱对H06-4环氧富锌/H53-13环氧云铁/丙烯酸聚氨脂、环氧富锌/厚膜灰云铁环氧/TB06-42丙烯酸聚氨脂和环氧防锈平整底漆/CE-46环氧/丙烯酸聚氨脂三种涂层体系进行了耐蚀性评价测试.结果表明,随着浸泡时间的延长,三种涂层体系的保护作用都降低.对比涂层的阻抗谱变化特征得知,H06-4环氧富锌/H53-13环氧云铁/丙烯酸聚氨脂涂层体系耐蚀性较佳,因此被选为某型装备用防腐蚀涂层.
Abstract
The corrosion resistance of three anti-corrosion coating systems including H06-4 zinc rich epoxy/H53-13 micaceous iron epoxy/acrylic polyurethane coating system,zinc rich epoxy/thick film gray micaceous iron epoxy/TB06-42 acrylic polyurethane coating system and epoxy anti-rust level priming/CE-46 epoxy/ acrylic polyurethane coating system was tested by the method of electrochemical impedance spectroscopy(EIS) for the corrosion protection of some special equipment.The results indicated that the protective effect of all three coating systems was reduced with increasing immersion time.H06-4 zinc rich epoxy/H53-13 micaceous iron epoxy/acrylic polyurethane coating system had the best corrosion resistance and was selected as the anti-corrosion coating system for the equipment.
中图分类号 TG174.46
所属栏目 试验研究
基金项目
收稿日期 2010/5/11
修改稿日期 2010/6/23
网络出版日期
作者单位点击查看
备注吴剑锋,硕士研究生.
引用该论文: WU Jian-feng,WANG Jie-liang,LV Tao,WANG Zhao-jun,SU Hai-tao. Corrosion Resistance of Three Coating Systems Studied by Electrochemical Impedance Spectroscopy[J]. Corrosion & Protection, 2010, 31(10): 760~762
被引情况:
【1】曾斌,侯峰,徐宏,王跃锋, "纳米SiO2粒子/镍基复合镀层腐蚀行为",腐蚀与防护 33, 222-225(2012)
【2】郭英,陈飞, "FBE与聚苯胺粉末共混涂层的防腐蚀性能",腐蚀与防护 33, 683-685(2012)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘旭文,熊金平,曹京宜,等.EIS法研究3种配套涂层体系的腐蚀电化学行为[J].化工学报,2008,59(3):659-664.
【2】Gray G S,Bernard R A.EIS:electrochemical impe-dance spectroscope a tool that can measure remaining life in protective coatings[C]//The Industrial Protective Coatings Conference and Exhibit.Floride,2003:209-227.
【3】杨丽霞.有机重防蚀涂层耐蚀性能研究[D].武汉:武汉材料保护研究所,2002.
【4】曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002.
【5】张鉴清,曹楚南.电化学阻抗谱方法研究评价有机涂层[J].腐蚀与防护,1998,19(3):99-104.
【6】毛肖,张九渊,薛进,等.热换器耐高温涂料的电化学阻抗谱特性分析[J].科技通报,2005,21(1):19-23.
【2】Gray G S,Bernard R A.EIS:electrochemical impe-dance spectroscope a tool that can measure remaining life in protective coatings[C]//The Industrial Protective Coatings Conference and Exhibit.Floride,2003:209-227.
【3】杨丽霞.有机重防蚀涂层耐蚀性能研究[D].武汉:武汉材料保护研究所,2002.
【4】曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002.
【5】张鉴清,曹楚南.电化学阻抗谱方法研究评价有机涂层[J].腐蚀与防护,1998,19(3):99-104.
【6】毛肖,张九渊,薛进,等.热换器耐高温涂料的电化学阻抗谱特性分析[J].科技通报,2005,21(1):19-23.
相关信息