溶解氧浓度对船体钢在海水中腐蚀行为的影响
Effect of Dissolved Oxygen on Corrosion Behavior of Hull Steels in Sea-water
摘 要
采用动电位极化、电化学阻抗谱(EIS)和失重试验,研究了海水中的溶解氧对1#、2#船体钢海水腐蚀行为的影响.极化曲线及电化学阻抗试验结果表明,随着海水中氧含量的升高,这两种船体钢的自腐蚀电位逐渐升高,腐蚀电流密度逐渐增大,腐蚀速率增大:失重试验表明,1#、2#钢在海水中的腐蚀类型主要为均匀腐蚀,且其腐蚀速率随溶解氧含量的增加而增大.
溶解氧
海水
腐蚀
hull steel
dissolved oxygen
seawater
corrosion
Abstract
Potentiodynamic polarization,electrochemical impedance spectroscopy (EIS) and weight loss method were used to study the effect of dissolved oxygen on corrosion behavior of 1# and 2# hull steels in sea water.The results showed that with increase of dissolved oxygen in seawater,corrosion potential increased,and both of corrosion current density and corrosion rate increased.The weight loss tests indicated that the hull steels suffered uniform corrosion in seawater.
中图分类号 TG172.5
所属栏目 试验研究
基金项目
收稿日期 2010/2/11
修改稿日期 2010/3/10
网络出版日期
作者单位点击查看
联系人作者傅晓蕾(xdlfxl@126.com)
备注傅晓蕾,硕士研究生.
引用该论文: FU Xiao-lei,MA Li,YAN Yong-gui,SUN Hao-fen. Effect of Dissolved Oxygen on Corrosion Behavior of Hull Steels in Sea-water[J]. Corrosion & Protection, 2010, 31(12): 942～945
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王佳,孟洁,唐晓,等.深海环境钢材腐蚀行为评价技术[J].中国腐蚀与防护学报,2007,27(1):1-7.
【2】朱相荣,王相润.金属材料的海洋腐蚀与防护[M].北京:国防工业出版社,1999:9-10.
【3】Magalhaes A A O,Margarit I C P,Mattos O R.Electrochemical characterization of chromate coatings on galvanized steel[J].Electrochimica Acta,1999,44(24):4281-4287.
【4】Azambuja D S,Martini E M A,Muller I L.Corrosion behavior of iron and AISI 304 stainless steel in tungstate aqueous solution containing chloride[J].Journal of the Brazilian Chemical Society,2003,14(4):570-576.
【5】张可敏,杨大智,邹建新,等.316L不锈钢强流脉冲电子束表面改性研究Ⅱ在模拟体液中的腐蚀行为[J].金属学报,2007,43(1):71-76.
【6】胡钢,许淳淳,池琳.X70管线钢在HCO-3/CO2-3体系中表面膜性能研究[J].腐蚀科学与防护技术,2005,17(5):331-334.
【7】黄运涛,彭乔.海水电解用金属氧化物阳极的失活机理[J].稀有金属材料与工程,2006,35(10):1610-1612.
【2】朱相荣,王相润.金属材料的海洋腐蚀与防护[M].北京:国防工业出版社,1999:9-10.
【3】Magalhaes A A O,Margarit I C P,Mattos O R.Electrochemical characterization of chromate coatings on galvanized steel[J].Electrochimica Acta,1999,44(24):4281-4287.
【4】Azambuja D S,Martini E M A,Muller I L.Corrosion behavior of iron and AISI 304 stainless steel in tungstate aqueous solution containing chloride[J].Journal of the Brazilian Chemical Society,2003,14(4):570-576.
【5】张可敏,杨大智,邹建新,等.316L不锈钢强流脉冲电子束表面改性研究Ⅱ在模拟体液中的腐蚀行为[J].金属学报,2007,43(1):71-76.
【6】胡钢,许淳淳,池琳.X70管线钢在HCO-3/CO2-3体系中表面膜性能研究[J].腐蚀科学与防护技术,2005,17(5):331-334.
【7】黄运涛,彭乔.海水电解用金属氧化物阳极的失活机理[J].稀有金属材料与工程,2006,35(10):1610-1612.
相关信息