成膜剂对黑色金属防锈水防锈性能的影响
Influence of Some Filmogens on Antirust Properties of Antirust Water for Ferrous Metal
摘 要
选取无水碳酸钠与三乙醇胺复配和无水碳酸钠与亚硝酸钠复配作为缓蚀剂.选取田菁胶、香豆胶、混合醇复合成膜剂等作为成膜剂.通过相容性和成膜性分析,筛选出了11种防锈水配方.大气暴露试验和湿热试验结果表明,成膜剂也对防锈水的防锈性能有较大影响,缓蚀剂与成膜剂的优化组合才能获得较好的防锈效果.本试验获得较好的防锈水配方为:复合成膜剂1%、亚硝酸钠6%、无水碳酸钠0.4%.
防锈水
成膜剂
缓蚀剂
ferrous metal
antirust water
filmogen
corrosion inhibitor
Abstract
Using compounds of anhydrous sodium carbonate and triethanolamine or anhydrous sodium carbonate and sodium nitrite as corrosion inhibitor,and sesbania gum,fenugreek gum,mixed alcohol and so on as filmogen,the eleven kinds of formulas were selected by analyzing the compatibility and film forming ability.The results of atmospheric exposure test and damp heat test showed that the effect of filmogen on antirust property of antirust water was considerable.The optimal formula of antirust water was composed of 1% compound filmogen,6% sodium nitrite and 0.4% anhydrous sodium carbonate.
中图分类号 TG174.42
所属栏目 应用技术
基金项目
收稿日期 2010/5/22
修改稿日期 2010/6/29
网络出版日期
作者单位点击查看
备注刘旭麟,副教授.
引用该论文: LIU Xu-lin,PENG Qiao,LIU Shun-hua,WEN Bin,LI Ting-ju,ZHANG Ming-jia. Influence of Some Filmogens on Antirust Properties of Antirust Water for Ferrous Metal[J]. Corrosion & Protection, 2010, 31(12): 970～972
被引情况:
【1】刘斌,金凯峰,谢建丽,刘涛,鲁俊东, "低浓度亚硝酸盐对A106B碳钢材料腐蚀的影响",腐蚀与防护 34, 228-231(2013)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】罗永秀,吴正前,王翠莲,等.F-124水基防锈剂的研究[J].腐蚀与防护,2001,22(4):149-150.
【2】刘旭麟,彭乔,刘顺华,等.一种不含亚硝酸钠的黑色金属防锈水的研制[J].铸造,2002,51(11):720-722.
【3】张天胜.缓蚀剂[M].北京:化学工业出版社,2002.
【4】张康复,萧怀斌,罗永秀,等.防锈材料应用手册[M].北京:化学工业出版社,2004.
【5】杨文庆.钼酸盐系缓蚀剂的进展[J].材料保护,1995,28(8):16-19.
【2】刘旭麟,彭乔,刘顺华,等.一种不含亚硝酸钠的黑色金属防锈水的研制[J].铸造,2002,51(11):720-722.
【3】张天胜.缓蚀剂[M].北京:化学工业出版社,2002.
【4】张康复,萧怀斌,罗永秀,等.防锈材料应用手册[M].北京:化学工业出版社,2004.
【5】杨文庆.钼酸盐系缓蚀剂的进展[J].材料保护,1995,28(8):16-19.
相关信息