低周疲劳试样裂纹在线检测法
The Method of On-Line NDT of Low Cycle Fatigue Specimen Cracks
摘 要
分别采用长焦显微镜观测法、银涂层判别法、声发射检测法和应变片检测法四种方法在TC18钛合金试样低周疲劳试验中进行在线检测,通过对比初始裂纹和裂纹长度的检测效果,对于类似试样可采用应变片检测法检测初始裂纹,对裂纹长度要求精度不高时可采用长焦显微镜观测法测量裂纹长度,测量精度要求较高时可采用银涂层法.
在线检测
裂纹长度记录
TC18钛合金
Low cycle fatigue
On line NDT
Crack length record
TC18 titanium alloy
Abstract
The telephoto microscope observation method,silver coating method,acoustic emission technique and strain gauge test method have been used for on-line NDT in the low cycle fatigue test of TC18 titanium alloy specimens.Comparing the detection results of the initial crack and the crack length,it shows that the strain gauge test method should be used to detect the initial crack and the telephoto microscope observation method can be used to observe the crack length in low accuracy;otherwise,the silver coating method is the best choice.
中图分类号 TG115.28 DOI 10.11973/wsjc201509005
所属栏目 科研成果与学术交流
基金项目
收稿日期 2014/11/5
修改稿日期
网络出版日期
作者单位点击查看
备注郑建军(1986-),男,工程师,主要从事飞机结构强度试验设计与分析工作.
引用该论文: ZHENG Jian-jun,ZHANG Zhao,WANG Qian,BAI Wei. The Method of On-Line NDT of Low Cycle Fatigue Specimen Cracks[J]. Nondestructive Testing, 2015, 37(9): 20～22
郑建军,张昭,王倩,白玮. 低周疲劳试样裂纹在线检测法[J]. 无损检测, 2015, 37(9): 20～22
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】仲维畅.中国无损检测简史[J].无损检测,2012,34(1):52-56.
【2】耿荣生,景鹏.绿色无损检测——NDT技术的未来发展之路[J].无损检测,2011,33(9):1-6.
【3】申雅峰,胡春燕,张磊.声发射技术在疲劳裂纹监测中的应用[J].无损检测,2012,34(8):34-38.
【4】樊鸿,张盛,王启智.应变片法确定混凝土动态起裂时间的研究[J].振动与冲击,2010,32(1):153-156.
【5】蒋洪伟.基于电阻应变片的结构健康监测实例[J].黑龙江水利科技,2012,34(8):49-51.
【2】耿荣生,景鹏.绿色无损检测——NDT技术的未来发展之路[J].无损检测,2011,33(9):1-6.
【3】申雅峰,胡春燕,张磊.声发射技术在疲劳裂纹监测中的应用[J].无损检测,2012,34(8):34-38.
【4】樊鸿,张盛,王启智.应变片法确定混凝土动态起裂时间的研究[J].振动与冲击,2010,32(1):153-156.
【5】蒋洪伟.基于电阻应变片的结构健康监测实例[J].黑龙江水利科技,2012,34(8):49-51.
相关信息