核电厂汽轮机低压转子叶片常见缺陷及其检测
Common Defects of Steam Turbine Low-pressure Rotor Blade in Nuclear Power Plant and Their Inspection Techniques
摘 要
高速旋转的汽轮机低压转子叶片是核电汽轮机组的重要部件之一,除了设计与制造缺陷外,运行期间还可能出现水蚀、共振、疲劳断裂等缺陷.深入分析了叶片常见缺陷及其产生原因,重点讨论了包括超声相控阵、荧光磁粉等在内的无损检验技术,可有效避免因叶片断裂导致的停机事件,为营运单位加强汽轮机叶片质量监督提供了重要参考.
叶片
缺陷
相控阵
Steam turbine
Blade
Defects
Phased array
Abstract
Water erosion damage,resonance vibration,fatigue fracture and other design or manufacture defects may occur on the steam turbine low-pressure rotor blade,which is one of the most important rotational equipments used in the nuclear power plants.This article analyzes the common defects of the blades and their causes,introduces ultrasonic phased array,fluorescent magnetic particle inspection and other non-destructive tests,which provides good references for the plants owners to improve the quality monitors of the steam turbine blade.
中图分类号 TG115.28 DOI 10.11973/wsjc201509017
所属栏目 实践经验
基金项目
收稿日期 2014/12/9
修改稿日期
网络出版日期
作者单位点击查看
备注尹峰(1971-),男,硕士,高级工程师,主要从事核电厂调试运行等工作.
引用该论文: YIN Feng,HONG Yuan-ping,DAI Heng-cai,QIU Wen-jun,LI Shi-wei,CHEN Qi-rong,CAO Feng. Common Defects of Steam Turbine Low-pressure Rotor Blade in Nuclear Power Plant and Their Inspection Techniques[J]. Nondestructive Testing, 2015, 37(9): 65～68
尹峰,洪源平,戴恒才,邱文军,李世伟,陈其荣,操丰. 核电厂汽轮机低压转子叶片常见缺陷及其检测[J]. 无损检测, 2015, 37(9): 65～68
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王江洪,齐琰,苏辉,等.电站汽轮机叶片疲劳断裂失效综述[J].汽轮机技术,1999,41(6):1-6.
【2】鄢宇鹏,孙弼,蔡颐年.汽轮机动叶片水蚀问题的研究[J].汽轮机技术,1994,36(5):305-310.
【3】程绍兵,刁伟辽.300 MW汽轮机叶片点蚀损伤机理分析及预防措施[J].热力发电,2003(12):46-47.
【4】李巍,李太江,王绍东,等.汽轮机末级动叶片水蚀损伤修复与防护试验研究[J].热力发电,2011,40(1):41-44.
【2】鄢宇鹏,孙弼,蔡颐年.汽轮机动叶片水蚀问题的研究[J].汽轮机技术,1994,36(5):305-310.
【3】程绍兵,刁伟辽.300 MW汽轮机叶片点蚀损伤机理分析及预防措施[J].热力发电,2003(12):46-47.
【4】李巍,李太江,王绍东,等.汽轮机末级动叶片水蚀损伤修复与防护试验研究[J].热力发电,2011,40(1):41-44.
相关信息