半固态Cu-Ni-Si合金压缩变形抗力的研究
Deforming Properties of Semi-solid Cu-Ni-Si Alloy
摘 要
采用Gleeble1500热模拟机对半固态Cu-Ni-Si合金进行了压缩变形抗力的研究,分析了不同微量元素、不同变形速率对该合金变形性能的影响.研究表明:添加0.05%铈元素对该合金的变形改善作用较好,微量硼元素则对合金的变形有阻碍作用.该半固态合金压缩变形的较佳工艺参数为:添加0.05％铈元素,保温温度1048℃,保温时间15s,变形速率为2s-1.
变形抗力
微量元素
变形速率
semi-solid copper alloy
deforming property
trace element
deformation rate
Abstract
The compressed deforming properties of Cu-Ni-Si alloy in semisolid state were studied using the Gleeble-1500 thermal simulator,and the effect of different trace elements and deformation rates on deforming properties of this alloy was analyzed.The deforming properties of Cu-Ni-Si alloy were improved preferably through adding 0.05%Ce.The adding of trace boron was harmful to deforming properties.The optimal process parameters for this semi-solid Cu-Ni-Si alloy were obtained as follows:0.05% Ce of addition,1048℃ of holding temperature,15s of holding time,and 2s-1of deformation rate.
中图分类号 TG146.1
所属栏目
基金项目 江西省自然科学基金资助项目(0050034)
收稿日期 2004/11/16
修改稿日期 2005/1/5
网络出版日期
作者单位点击查看
备注刘勇(1980-),男,江西于都人,硕士研究生.
引用该论文: LIU Yong,YANG Xiang-jie,LU De-ping,HAN Li-hua. Deforming Properties of Semi-solid Cu-Ni-Si Alloy[J]. Materials for mechancial engineering, 2006, 30(2): 51～53
刘勇,杨湘杰,陆德平,韩丽华. 半固态Cu-Ni-Si合金压缩变形抗力的研究[J]. 机械工程材料, 2006, 30(2): 51～53
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Flemings M C.Behavior of metal alloys in the semi-solid state[J].Met trans B,1991,(6):957-981.
【2】杨湘杰,韩丽华,谢水生.铝合金触变成形技术及其应用[J].江西科学,1999,17(4):261-268.
【3】谢水生,黄声宏.半固态金属加工技术及其应用[M].北京:冶金工业出版社,1999.
【4】Chen C P,Tsao C-Y.Aemi-solid deformation of A356 Al alloys[A].Proceedings of the 4th International Conference on Semi-solid Processing of Alloys and Composites[C].Sheffield:SRP Ltd,1996.16-20.
【5】洛阳铜加工厂中心试验室金相组.铜及铜合金金相图谱[M].北京:冶金工业出版社,1983.
【6】熊军,杨湘杰,刘勇.液固两相区等温处理对Al-Mg-Si合金力学性能的影响[J].铸造,2003,(9):691-694.
【7】张大辉,毛卫民,钟雪友.变形速率对半固态AlSi7Mg合金变形性的影响[J].中国有色金属学报,2000,10(增):132-134.
【8】陈晓阳.半固态亚共晶Al-7.0Si合金触变特性的研究[D].北京:北京科技大学,1998.37.
【9】张大辉,毛卫民,钟雪友.半固态AlSi7Mg合金触变压缩过程中变形性的研究.第一届半固态金属加工技术研讨会论文集[C].北京:中国机械工程学会,2000.
【2】杨湘杰,韩丽华,谢水生.铝合金触变成形技术及其应用[J].江西科学,1999,17(4):261-268.
【3】谢水生,黄声宏.半固态金属加工技术及其应用[M].北京:冶金工业出版社,1999.
【4】Chen C P,Tsao C-Y.Aemi-solid deformation of A356 Al alloys[A].Proceedings of the 4th International Conference on Semi-solid Processing of Alloys and Composites[C].Sheffield:SRP Ltd,1996.16-20.
【5】洛阳铜加工厂中心试验室金相组.铜及铜合金金相图谱[M].北京:冶金工业出版社,1983.
【6】熊军,杨湘杰,刘勇.液固两相区等温处理对Al-Mg-Si合金力学性能的影响[J].铸造,2003,(9):691-694.
【7】张大辉,毛卫民,钟雪友.变形速率对半固态AlSi7Mg合金变形性的影响[J].中国有色金属学报,2000,10(增):132-134.
【8】陈晓阳.半固态亚共晶Al-7.0Si合金触变特性的研究[D].北京:北京科技大学,1998.37.
【9】张大辉,毛卫民,钟雪友.半固态AlSi7Mg合金触变压缩过程中变形性的研究.第一届半固态金属加工技术研讨会论文集[C].北京:中国机械工程学会,2000.
相关信息