电磁搅拌合成(Al2O3+Al3Zr)p/Al复合材料的净化机制与性能
Mechanism and Properties of Fabricating and Cleaning-up for (Al2O3+Al3Zr)p/Al Composites with Electromagnetic Stirring
摘 要
在电磁搅拌条件下,通过Al-Zr(CO3)2熔体原位反应法,合成了Al2O3、Al3Zr颗粒增强铝基复合材料,对材料的组织和性能进行了研究.结果表明：由于电磁搅拌能促进铝热反应固液两相的传质和扩散,改善了原位合成动力学条件,采用电磁搅拌合成的复合材料中增强相颗粒在基体中的体积分数和弥散度都较未施加电磁搅拌时有了明显提高,浇注缺陷明显减少,铝基体得到净化;当Zr(CO3)2加入量为20％时,所获复合材料抗拉强度达202.6MPa,较未施加电磁搅拌的强度提高了34.8％.
原位反应
合成净化
拉伸性能
electromagnetic stirring
in-situ reaction
cleaning up
tensile property
Abstract
Under the condition of electromagnetic stirring(EMS),the composites of Al2O3、Al3Zr particulates reinforced aluminum matrix was synthesized by Al-Zr(CO3)2 components through the direct melt in-situ reaction method.The microstructure and properties of composites were studied.The mass transfer and diffuseness in solid-liquid phases could be accelerated by EMS and in-situ reactions were improved largely.The fraction volume of particulates in aluminum matrix was enhanced and the particulates were well distributed in the matrix.Casting defects were dramatically decreased,which led to a high cleanness of aluminum matrix.When the added amount of Zr(CO3)2 was 20%,the tensile strength was 202.6MPa,which was increased by 34.8％ compared to that of samples fabricated without electromagnetic stirring.
中图分类号 TB331
所属栏目
基金项目 江苏省“十五”科技攻关资助项目(BE2002039);江苏省高技术研究资助项目(BG2005026)
收稿日期 2005/1/20
修改稿日期 2005/11/11
网络出版日期
作者单位点击查看
备注李桂荣(1976-),女,江苏镇江人,讲师,博士研究生.
引用该论文: LI Gui-rong,ZHAO Yu-tao,DAI Qi-xun,CHEN Xiao-nong,CAO Jian-feng,BAI Li-qing. Mechanism and Properties of Fabricating and Cleaning-up for (Al2O3+Al3Zr)p/Al Composites with Electromagnetic Stirring[J]. Materials for mechancial engineering, 2006, 30(4): 37～40
李桂荣,赵玉涛,戴起勋,程晓农,曹健峰,柏立庆. 电磁搅拌合成(Al2O3+Al3Zr)p/Al复合材料的净化机制与性能[J]. 机械工程材料, 2006, 30(4): 37～40
被引情况:
【1】祝晓辉,赵玉涛,李桂荣,陈刚,佘昌俊,轩动华,郑梦, "高频磁场下原位合成Al3(Ti0.5Zr0.5)p/6005A复合材料的显微组织与性能",机械工程材料 35, 71-75(2011)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Lioyd D J.Particle reinforced aluminum magnesium matrix composites[J].International Materials Revieurs,1994,39(1):1-22.
【2】Feest E A,Kyoung R M.Who can profit from the use of metal matrix composites[J].Metallurgia,1996,(3):113-119.
【3】HUANG Zan-jun.Study of in-situ Al2O3 particulate reinforcement aluminum-based composites[J].Acta Metallurgica Sinica,2002,6:568-574.
【4】陈子勇,陈玉勇,舒群,等.熔体反应法制备Al-4.5Cu/TiB2复合材料的热力学[J].材料研究学报,2000,14(1):68-74.
【5】赵玉涛,孙国雄.Al-ZrOCl2反应体系制备ZrAl3(p)+Al2O3(p)/Al复合材料[J].中国有色金属学报,2001,11(2):41-46.
【6】Zhang Edin,Zeng Xiaochun,Zeng Songyan.Microstructure and property of Al/TiC composites prepared by reaction systhesis[J].Trans Nonferrous Met Soc China,1999,6(1):114-119.
【7】黄希祜.钢铁冶金原理[M].北京:冶金工业出版社,2002.278.
【8】Griffiths W D,Mc Cartney D G.The effect of electromagnetic stirring during solidification on structure of Al-Si alloys[J].Materials Science and Engineering,1996,A216:47-60.
【9】Griffiths W D,Mc Cartney D G.The effect of electromagnetic stirring on macrostructure and macrosegreation in the aluminum alloy 7150[J].Matericals Science and Engineering,1997,A222:140-148.
【10】邱竹贤.有色金属冶金学[M].沈阳:东北大学出版社,2001.
【11】ZHAO Yu-tao,LI Zhong-hua,CHENG Xiao-nong,et al.In-situ synthesizes ZrAl3(p)+Al2O3(p)/A356 composites by direct melt reaction in Al-Zr-O system[J].Trans Nonferrous Met Soc China,2003,13(4):769-773.
【2】Feest E A,Kyoung R M.Who can profit from the use of metal matrix composites[J].Metallurgia,1996,(3):113-119.
【3】HUANG Zan-jun.Study of in-situ Al2O3 particulate reinforcement aluminum-based composites[J].Acta Metallurgica Sinica,2002,6:568-574.
【4】陈子勇,陈玉勇,舒群,等.熔体反应法制备Al-4.5Cu/TiB2复合材料的热力学[J].材料研究学报,2000,14(1):68-74.
【5】赵玉涛,孙国雄.Al-ZrOCl2反应体系制备ZrAl3(p)+Al2O3(p)/Al复合材料[J].中国有色金属学报,2001,11(2):41-46.
【6】Zhang Edin,Zeng Xiaochun,Zeng Songyan.Microstructure and property of Al/TiC composites prepared by reaction systhesis[J].Trans Nonferrous Met Soc China,1999,6(1):114-119.
【7】黄希祜.钢铁冶金原理[M].北京:冶金工业出版社,2002.278.
【8】Griffiths W D,Mc Cartney D G.The effect of electromagnetic stirring during solidification on structure of Al-Si alloys[J].Materials Science and Engineering,1996,A216:47-60.
【9】Griffiths W D,Mc Cartney D G.The effect of electromagnetic stirring on macrostructure and macrosegreation in the aluminum alloy 7150[J].Matericals Science and Engineering,1997,A222:140-148.
【10】邱竹贤.有色金属冶金学[M].沈阳:东北大学出版社,2001.
【11】ZHAO Yu-tao,LI Zhong-hua,CHENG Xiao-nong,et al.In-situ synthesizes ZrAl3(p)+Al2O3(p)/A356 composites by direct melt reaction in Al-Zr-O system[J].Trans Nonferrous Met Soc China,2003,13(4):769-773.
相关信息