钢纤维长径比对钢纤维聚合物混凝土抗弯性能的影响
Influence of Steel-fiber Long-diameter Ratio on Bending Strength of Steel-fiber Polymer Concrete
摘 要
采用单点集中加载方法研究了钢纤维聚合物混凝土中钢纤维的长径比对其抗弯性能的影响.结果表明：向聚合物混凝土中加入适量钢纤维可提高其抗弯强度和韧性;当钢纤维长径比为70、含量为48kg/m3时,钢纤维聚合物混凝土的抗弯强度较大,韧性较好.
长径比
抗弯性能
steel-fiber polymer concrete
long-diameter ratio
bending strength
Abstract
The influence of long-diameter ratio of steel-fiber on bending properties of the steel-fiber polymer concrete was studied using single-point loading method.An appropriate amount of steel-fiber could improve the bending strength and toughness of the polymer concrete;When long-diameter ratio was 70 and quantity contained was 48kg/m3,the bending strength of steel-fiber polymer concrete was the biggest and the toughness was the best.
中图分类号 TU528.41
所属栏目
基金项目 辽宁省教育厅高等学校科研基金资助项目(20081226)
收稿日期 2005/1/11
修改稿日期 2005/3/26
网络出版日期
作者单位点击查看
备注徐平(1964-),男,辽宁阜新人,教授,博士.
引用该论文: XU Ping,WANG Ming-xu,PAN Yi-shan. Influence of Steel-fiber Long-diameter Ratio on Bending Strength of Steel-fiber Polymer Concrete[J]. Materials for mechancial engineering, 2006, 30(4): 54～55
徐平,王明旭,潘一山. 钢纤维长径比对钢纤维聚合物混凝土抗弯性能的影响[J]. 机械工程材料, 2006, 30(4): 54～55
被引情况:
【1】白文峰,张建华,闫鹏,汪心立,段彩云, "玻璃纤维增强聚合物混凝土的抗压强度",机械工程材料 32, 30-33(2008)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】胡果明,张绍勇,周倜.树脂混凝土在机床基础件上的应用[J].机床,1993,(10):8-10.
【2】徐平,崔剑.纤维聚合物混凝土高阻尼性及其在机床制造业中的应用[J].机床与液压,2004,(4):103-105.
【3】徐平,崔剑.纤维长径比和含量对钢纤维聚合物混凝土抗压强度的影响[J].机械制造,2004,(10):60-61.
【4】姚秉华,李德信,应锦春.人造花岗岩复合材料的研究及应用[J].机械工程材料,1993,17(4):37-39.
【5】姜福田.混凝土力学性能与测试[M].北京:中国铁道出版社,1989.
【6】ASTM C1018-1989,ASTM Standardes for concrete and mineral aggregates[S].
【2】徐平,崔剑.纤维聚合物混凝土高阻尼性及其在机床制造业中的应用[J].机床与液压,2004,(4):103-105.
【3】徐平,崔剑.纤维长径比和含量对钢纤维聚合物混凝土抗压强度的影响[J].机械制造,2004,(10):60-61.
【4】姚秉华,李德信,应锦春.人造花岗岩复合材料的研究及应用[J].机械工程材料,1993,17(4):37-39.
【5】姜福田.混凝土力学性能与测试[M].北京:中国铁道出版社,1989.
【6】ASTM C1018-1989,ASTM Standardes for concrete and mineral aggregates[S].
相关信息