常用压力容器钢断裂行为研究
Fracture Behaviors of Several Pressure Vessel Steels
摘 要
利用三点弯曲试验,测试了16MnR、20R和Q235B三种常用压力容器钢的断裂行为和断裂韧度,并用扫描电镜观察了试样的断口形貌.结果表明：三种材料常温下均呈现韧性断裂,所有试样断口均存在裂纹分层现象,其中以16MnR裂纹扩展区分层现象最不明显,而Q235B裂纹扩展区分层现象最明显;当裂纹扩展方向与分层方向不一致时,分层现象的存在阻止了裂纹的扩展,从而提高材料的强度与韧度.
断裂韧度
裂纹扩展区
pressure vessel steel
fracture toughness
crack extension zone
Abstract
The fracture toughness of 16MnR,20R and Q235B steel specimens were investigated respectively using three-point-bending experiments,and the fracture surface morphology was observed by SEM.The three samples exhibited ductile rupture behavior at room temperature.Delaminating phenomenon was observed in fracture zone of the three samples,but the delaminating phenomenon of fracture of 16MnR steel was obscure,while that of Q235B steel was obvious.When the direction of crack delaminating phenomena was not consistent with the direction of crack propagation,the delaminating phenomena provided resistance to the crack propagation,which increases the strength and toughness properties of the samples.
中图分类号 TK229.1 TG115.5
所属栏目
基金项目
收稿日期 2005/1/24
修改稿日期 2005/5/28
网络出版日期
作者单位点击查看
备注李亚宁(1982-),女,山西运城人,硕士研究生.
引用该论文: LI Ya-ning,DONG Bao-sheng,ZHAO Xin-wei,LUO Jin-heng,ZHOU Gen-shu,ZHENG Mao-sheng. Fracture Behaviors of Several Pressure Vessel Steels[J]. Materials for mechancial engineering, 2006, 30(4): 70～72
李亚宁,董保胜,赵新伟,罗金恒,周根树,郑茂盛. 常用压力容器钢断裂行为研究[J]. 机械工程材料, 2006, 30(4): 70～72
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李志安.金志浩.宫殿民.等.压力容器断裂理论与缺陷评定[M].大连:大连理工大学出版社,1994.
【2】王志文,李培宁,雷月葆,等.我国压力容器通用失效评定曲线的初步研究[J].化工机械,1994,22(2):115-124.
【3】Neimitz A,Dzioba I,Ga kiewicz J,et al.A study of stable crack growth using experimental methods,finite elements and fractography[J].Engineering Fracture Mechanics,2004,71:1325-1355.
【4】董惠茹,郭万林,罗金恒.油气输送管线钢得分层机理及其对断裂的影响[J].机械工程材料,2003,27(7):9-11.
【5】郭万林,董惠茹,杨政,等.厚度与分层耦合效应对管线钢断裂韧性的影响[J].金属学报,2001,37(4):386-390.
【6】库默,杰曼,施.弹塑性断裂分析工程方法(EPRI报告NP-1931)[M].北京:国防工业出版社,1985.
【7】王杰,徐金记,陶宏锦.柔度法在材料低温断裂韧性试验中的应用研究[J].机械工程材料,1998,22(1):51-53.
【8】冯耀荣,李鹤林,杜百平,等.应力状态、温度和腐蚀介质对X52ERW输送管断裂韧性的影响[J].机械工程材料,1999,23(6):12-14.
【2】王志文,李培宁,雷月葆,等.我国压力容器通用失效评定曲线的初步研究[J].化工机械,1994,22(2):115-124.
【3】Neimitz A,Dzioba I,Ga kiewicz J,et al.A study of stable crack growth using experimental methods,finite elements and fractography[J].Engineering Fracture Mechanics,2004,71:1325-1355.
【4】董惠茹,郭万林,罗金恒.油气输送管线钢得分层机理及其对断裂的影响[J].机械工程材料,2003,27(7):9-11.
【5】郭万林,董惠茹,杨政,等.厚度与分层耦合效应对管线钢断裂韧性的影响[J].金属学报,2001,37(4):386-390.
【6】库默,杰曼,施.弹塑性断裂分析工程方法(EPRI报告NP-1931)[M].北京:国防工业出版社,1985.
【7】王杰,徐金记,陶宏锦.柔度法在材料低温断裂韧性试验中的应用研究[J].机械工程材料,1998,22(1):51-53.
【8】冯耀荣,李鹤林,杜百平,等.应力状态、温度和腐蚀介质对X52ERW输送管断裂韧性的影响[J].机械工程材料,1999,23(6):12-14.
相关信息